Multiwalled carbon nanotubes (MWCNTs) mixed in poly(3-hexylthiophene) (P3HT) were used as a photoactive layer for organic solar cells (OSC). The flexible OSCs of a structure of PET/rGO-P3HT/P3CT/PCBM/LiF-Al were prepa...Multiwalled carbon nanotubes (MWCNTs) mixed in poly(3-hexylthiophene) (P3HT) were used as a photoactive layer for organic solar cells (OSC). The flexible OSCs of a structure of PET/rGO-P3HT/P3CT/PCBM/LiF-Al were prepared by spincoating. The UV-Vis absorption spectra of the photoactive films and current-voltage characteristics of the OSCs showed the advantage of the composite devices above the pristine-polymeric ones. Under illumination of light with a 100 mW/cm<sup>2</sup>-powerdensity, the photoelectrical conversion efficiency (PCE) of the OSCs with 3.0 wt% MWNCTs embedded in the photoactive layer possess a value as large as 2.35%. The obtained results suggest further useful applications of the flexible large-area solar cells.展开更多
With the aim of producing simple and effective transparent conducting electrodes, the conducting polymer poly(3-hexylthiophene) (P3HT) incorporated with reduced graphene oxide film (rGO) (called rGO-P3HT) was prepared...With the aim of producing simple and effective transparent conducting electrodes, the conducting polymer poly(3-hexylthiophene) (P3HT) incorporated with reduced graphene oxide film (rGO) (called rGO-P3HT) was prepared by spin-coating method. Structural, electrical and optical characterization showed that rGO-P3HT films 9.0 wt% P3HT exhibited good stability when exposed to the ambient atmosphere. These composite films of 200 nm thickness possess a sheet resistance and transparency of R□~ 17Ω and T ~ 72%, respectively. Owing to containing conducting polymer, rGO-P3HT-coated glass could be efficiently used in photovoltaic applications, in organic solar cells in particular, with the replacement of the indium tin oxide (ITO) and fluorine tin oxide (FTO) electrodes.展开更多
文摘Multiwalled carbon nanotubes (MWCNTs) mixed in poly(3-hexylthiophene) (P3HT) were used as a photoactive layer for organic solar cells (OSC). The flexible OSCs of a structure of PET/rGO-P3HT/P3CT/PCBM/LiF-Al were prepared by spincoating. The UV-Vis absorption spectra of the photoactive films and current-voltage characteristics of the OSCs showed the advantage of the composite devices above the pristine-polymeric ones. Under illumination of light with a 100 mW/cm<sup>2</sup>-powerdensity, the photoelectrical conversion efficiency (PCE) of the OSCs with 3.0 wt% MWNCTs embedded in the photoactive layer possess a value as large as 2.35%. The obtained results suggest further useful applications of the flexible large-area solar cells.
文摘With the aim of producing simple and effective transparent conducting electrodes, the conducting polymer poly(3-hexylthiophene) (P3HT) incorporated with reduced graphene oxide film (rGO) (called rGO-P3HT) was prepared by spin-coating method. Structural, electrical and optical characterization showed that rGO-P3HT films 9.0 wt% P3HT exhibited good stability when exposed to the ambient atmosphere. These composite films of 200 nm thickness possess a sheet resistance and transparency of R□~ 17Ω and T ~ 72%, respectively. Owing to containing conducting polymer, rGO-P3HT-coated glass could be efficiently used in photovoltaic applications, in organic solar cells in particular, with the replacement of the indium tin oxide (ITO) and fluorine tin oxide (FTO) electrodes.