Selective synthesis of ethanol from syngas under the Co-based catalysts is still challenging due to the hard of regulating the active site Co^(0) and Co^(2+)ratio.In this work,a series of CaTi_(0.9-x)Co_(x)Mo_(0.1)O_(...Selective synthesis of ethanol from syngas under the Co-based catalysts is still challenging due to the hard of regulating the active site Co^(0) and Co^(2+)ratio.In this work,a series of CaTi_(0.9-x)Co_(x)Mo_(0.1)O_(3)(x=0,0.1-0.4)and CaTi_(0.7)Co_(0.3)O_(3) catalysts were prepared by using citric acid complexation method to promote the synthesis of ethanol.It was found that Mo species in the perovskite lattice can regulate the Co^(0) and Co^(2+)ratio through the domain-limiting effect of perovskite and the degree of Co reduction could be adjusted by changing the Co/Mo molar ratio.Among these investigated catalysts,the total selectivity of alcohols over the catalyst with the optimal Co/Mo ratio CaTi_(0.6)Co_(0.3)Mo_(0.1)O_(3) reached 39.1%,with ethanol accounting for 74.7%,which was ascribed to the moderate and tightly bound ratio of dissociative to non-dissociative adsorption sites on the surface and the balance of CH_(x)-CH_(y) coupling and C^(O) insertion.展开更多
基金National Natural Science Foundation of China(21872101,21962014)Science and Technology Program of Zungeer County,Inner Mongolia(2020YY-12)。
文摘Selective synthesis of ethanol from syngas under the Co-based catalysts is still challenging due to the hard of regulating the active site Co^(0) and Co^(2+)ratio.In this work,a series of CaTi_(0.9-x)Co_(x)Mo_(0.1)O_(3)(x=0,0.1-0.4)and CaTi_(0.7)Co_(0.3)O_(3) catalysts were prepared by using citric acid complexation method to promote the synthesis of ethanol.It was found that Mo species in the perovskite lattice can regulate the Co^(0) and Co^(2+)ratio through the domain-limiting effect of perovskite and the degree of Co reduction could be adjusted by changing the Co/Mo molar ratio.Among these investigated catalysts,the total selectivity of alcohols over the catalyst with the optimal Co/Mo ratio CaTi_(0.6)Co_(0.3)Mo_(0.1)O_(3) reached 39.1%,with ethanol accounting for 74.7%,which was ascribed to the moderate and tightly bound ratio of dissociative to non-dissociative adsorption sites on the surface and the balance of CH_(x)-CH_(y) coupling and C^(O) insertion.