The Sodium Montmorillonite(Na-MMT)is not susceptible to polymer due to its organophilic character and low basal spacing.The primary objective of this study was to improve Na-MMT platelets separation by organically mod...The Sodium Montmorillonite(Na-MMT)is not susceptible to polymer due to its organophilic character and low basal spacing.The primary objective of this study was to improve Na-MMT platelets separation by organically modifying it with cation and anion exchanges using Cetyl trimethyl ammonium bromide(CTAB)and Sodium dodecyl sulfate(SDS)respectively.Basal spacing,presence of functional groups,Zetapotential with particle size analysis and thermal stability of the Organomodified Na-MMT(OMMT)were characterized using XRD,FTIR,zeta-potential analyzer and TGA respectively.The basal spacing of CTAB modified OMMTincreased to 19.5Åfrom 11.0Åwhich corresponds to the basal spacing of Na-MMT.The SDS modified OMMT did not show any increase in the basal spacing.FTIR spectra of CTAB modified Na-MMT illustrated the attachment of CTAB functional groups to Na-MMT,while the same was absent in the case of SDS modified Na-MMT.The zeta-potential of Na-MMT shifted from–24.88 mV to 15.66 mV in the case of CTAB modified Na-MMTand 12.49 mV for SDS modified Na-MMT,indicating a greater surface potential of the modified nanoclay.The TGA showed greater weight loss for CTAB modified Na-MMT than that for Na-MMT,indicating the effective Na+ion exchange with alkyl amines.展开更多
The dispersion of montmorillonite （MMT） in vinylester for preparing nanoclay/vinylester gel coat was reported. Two sets of MMT/vinylester specimens, namely Type I and Type 2, were prepared for comparative studies. T...The dispersion of montmorillonite （MMT） in vinylester for preparing nanoclay/vinylester gel coat was reported. Two sets of MMT/vinylester specimens, namely Type I and Type 2, were prepared for comparative studies. Type I specimens were prepared using ultrasonication only, and Type 2 specimens were prepared using both ultrasonication and twin-screw extrusion. According to XRD and TEM results, Type 2 specimens showed lower levels of nanoclay agglomeration and higher levels o! exfoliation. DSC results showed that the glass transition temperatures of Type 2 specimens are higher than those of Type 1 specimens. TGA results showed that the residual weight of 4 wt.% MMT/vinylester of Type 1 was 7.38%, while the corresponding value of Type 2 was 13,5%, indicating lower thermal degradation in the latter. MMTt vinylester/glass and MMT/vinylester/carbon specimens were fabricated and tested for mechanical and fire retardation behaviours. Type 2 based nanocomposite laminates showed greater values of ultimate tensile strength, flexural strength, interlaminar shear strength, impact strength, horizontal burning rate, and vertical burning rate than Type 1 based laminates. SEM images of tensile fractured surfaces revealed that Type 2 based laminates have no or less agglomeration of nanoclay than Type 1 based laminates.展开更多
文摘The Sodium Montmorillonite(Na-MMT)is not susceptible to polymer due to its organophilic character and low basal spacing.The primary objective of this study was to improve Na-MMT platelets separation by organically modifying it with cation and anion exchanges using Cetyl trimethyl ammonium bromide(CTAB)and Sodium dodecyl sulfate(SDS)respectively.Basal spacing,presence of functional groups,Zetapotential with particle size analysis and thermal stability of the Organomodified Na-MMT(OMMT)were characterized using XRD,FTIR,zeta-potential analyzer and TGA respectively.The basal spacing of CTAB modified OMMTincreased to 19.5Åfrom 11.0Åwhich corresponds to the basal spacing of Na-MMT.The SDS modified OMMT did not show any increase in the basal spacing.FTIR spectra of CTAB modified Na-MMT illustrated the attachment of CTAB functional groups to Na-MMT,while the same was absent in the case of SDS modified Na-MMT.The zeta-potential of Na-MMT shifted from–24.88 mV to 15.66 mV in the case of CTAB modified Na-MMTand 12.49 mV for SDS modified Na-MMT,indicating a greater surface potential of the modified nanoclay.The TGA showed greater weight loss for CTAB modified Na-MMT than that for Na-MMT,indicating the effective Na+ion exchange with alkyl amines.
文摘The dispersion of montmorillonite （MMT） in vinylester for preparing nanoclay/vinylester gel coat was reported. Two sets of MMT/vinylester specimens, namely Type I and Type 2, were prepared for comparative studies. Type I specimens were prepared using ultrasonication only, and Type 2 specimens were prepared using both ultrasonication and twin-screw extrusion. According to XRD and TEM results, Type 2 specimens showed lower levels of nanoclay agglomeration and higher levels o! exfoliation. DSC results showed that the glass transition temperatures of Type 2 specimens are higher than those of Type 1 specimens. TGA results showed that the residual weight of 4 wt.% MMT/vinylester of Type 1 was 7.38%, while the corresponding value of Type 2 was 13,5%, indicating lower thermal degradation in the latter. MMTt vinylester/glass and MMT/vinylester/carbon specimens were fabricated and tested for mechanical and fire retardation behaviours. Type 2 based nanocomposite laminates showed greater values of ultimate tensile strength, flexural strength, interlaminar shear strength, impact strength, horizontal burning rate, and vertical burning rate than Type 1 based laminates. SEM images of tensile fractured surfaces revealed that Type 2 based laminates have no or less agglomeration of nanoclay than Type 1 based laminates.
