Different oxygen and nitrogen containing functional groups were created on the surface of the multiwalled carbon nanotubes. The multi-walled carbon nanotubes were treated in ultrasonic bath with sulfuric or nitric aci...Different oxygen and nitrogen containing functional groups were created on the surface of the multiwalled carbon nanotubes. The multi-walled carbon nanotubes were treated in ultrasonic bath with sulfuric or nitric acid. Furthermore the surface texture was modified by increase of the roughness. In particular after treatment with the oxidizing nitric acid, in comparison to the H2SO4 or ultra-sonic treated samples,craters and edges are dominating the surface structures. Manganese oxide was deposited on the multiwalled carbon nanotubes by precipitation mechanism. Various manganese oxides are formed during the deposition process. The samples were characterized by elemental analysis, microscopy, thermal analysis,Raman spectroscopy, and by the zeta potential as well as X-ray diffraction measurements. It was shown that the deposited manganese oxides are stabilized rather by surface texture of the multi-walled carbon nanotubes than by created functional groups.展开更多
Raman spectroscopy is a common method of studying carbon-based materials such as multi-walled carbon nanotubes (MWCNT). However, the analysis of this technique is non-trivial since recorded spectra may be a convolutio...Raman spectroscopy is a common method of studying carbon-based materials such as multi-walled carbon nanotubes (MWCNT). However, the analysis of this technique is non-trivial since recorded spectra may be a convolution of both molecular vibrations and phonon resonances. The energies of these physical processes may occur in the same energy regime, and hence several analytical approaches can be necessary for a full analysis. Due to the negligible quantities of non-graphitic carbon in MWCNT, the present fitting procedure focuses on understanding phonon resonances to elucidate how varying modifications of MWCNT ultimately influence their graphitic bulk structure. We have found this approach to provide greater insight into the structure of MWCNT when low quantities of amorphous carbon are present, when compared with methods which try to interpret both phonon scattering and molecular vibrations simultaneously. Different pre-treatments for the modification of the graphitic structure of MWCNT are compared, including aqueous acidic and gas phase methods, and statistically evaluated. Focusing on phonon resonances enables one to analyze the reaction process of nitrosulfuric acid pre-treatment at different temperatures. Thereby, it is possible to control the ratio between defects and graphitic structures in MWCNT samples and prepare samples with reproducible D/G ratios.展开更多
文摘Different oxygen and nitrogen containing functional groups were created on the surface of the multiwalled carbon nanotubes. The multi-walled carbon nanotubes were treated in ultrasonic bath with sulfuric or nitric acid. Furthermore the surface texture was modified by increase of the roughness. In particular after treatment with the oxidizing nitric acid, in comparison to the H2SO4 or ultra-sonic treated samples,craters and edges are dominating the surface structures. Manganese oxide was deposited on the multiwalled carbon nanotubes by precipitation mechanism. Various manganese oxides are formed during the deposition process. The samples were characterized by elemental analysis, microscopy, thermal analysis,Raman spectroscopy, and by the zeta potential as well as X-ray diffraction measurements. It was shown that the deposited manganese oxides are stabilized rather by surface texture of the multi-walled carbon nanotubes than by created functional groups.
文摘Raman spectroscopy is a common method of studying carbon-based materials such as multi-walled carbon nanotubes (MWCNT). However, the analysis of this technique is non-trivial since recorded spectra may be a convolution of both molecular vibrations and phonon resonances. The energies of these physical processes may occur in the same energy regime, and hence several analytical approaches can be necessary for a full analysis. Due to the negligible quantities of non-graphitic carbon in MWCNT, the present fitting procedure focuses on understanding phonon resonances to elucidate how varying modifications of MWCNT ultimately influence their graphitic bulk structure. We have found this approach to provide greater insight into the structure of MWCNT when low quantities of amorphous carbon are present, when compared with methods which try to interpret both phonon scattering and molecular vibrations simultaneously. Different pre-treatments for the modification of the graphitic structure of MWCNT are compared, including aqueous acidic and gas phase methods, and statistically evaluated. Focusing on phonon resonances enables one to analyze the reaction process of nitrosulfuric acid pre-treatment at different temperatures. Thereby, it is possible to control the ratio between defects and graphitic structures in MWCNT samples and prepare samples with reproducible D/G ratios.