This study compares the effect of treated pineapple leaves fibres (T-PALF) with sodium hydroxide solution and untreated fibres (N-PALF) on the compressive and flexural strength of earth bricks stabilized with 3% and 5...This study compares the effect of treated pineapple leaves fibres (T-PALF) with sodium hydroxide solution and untreated fibres (N-PALF) on the compressive and flexural strength of earth bricks stabilized with 3% and 5% cement. The fibre content ranged from 0% to 5% in steps of 1% by weight. The compressive strength tests were made at 7, 14, 21 and 28 days of curing;the flexural strength test were conducted at 28th day only. The results show that the T-PALF had a higher compressive strength when comparing to the N-PALF. The highest compressive strength of the bricks was obtained at 28 days of curing. The compressive strength at 28 days of stabilized brick at 3% and 5% of cement reinforced with T-PALF were 4.01 and 4.81 MPa, respectively, while the one reinforced with N-PALF was 3.19 and 4.63 MPa, respectively. The results further show that the highest flexural strength of both stabilized bricks at 3% and 5% of cement reinforced with T-PALF and N-PALF was obtained with the bricks stabilized with 5% of cement reinforced with T-PALF. This results show that bricks stabilized with 5% cement and reinforced with 3% of treated fibres content are good for construction of load bearing walls. It was observed;a significant improvement of the reinforced blocks under flexure than under compression.展开更多
文摘This study compares the effect of treated pineapple leaves fibres (T-PALF) with sodium hydroxide solution and untreated fibres (N-PALF) on the compressive and flexural strength of earth bricks stabilized with 3% and 5% cement. The fibre content ranged from 0% to 5% in steps of 1% by weight. The compressive strength tests were made at 7, 14, 21 and 28 days of curing;the flexural strength test were conducted at 28th day only. The results show that the T-PALF had a higher compressive strength when comparing to the N-PALF. The highest compressive strength of the bricks was obtained at 28 days of curing. The compressive strength at 28 days of stabilized brick at 3% and 5% of cement reinforced with T-PALF were 4.01 and 4.81 MPa, respectively, while the one reinforced with N-PALF was 3.19 and 4.63 MPa, respectively. The results further show that the highest flexural strength of both stabilized bricks at 3% and 5% of cement reinforced with T-PALF and N-PALF was obtained with the bricks stabilized with 5% of cement reinforced with T-PALF. This results show that bricks stabilized with 5% cement and reinforced with 3% of treated fibres content are good for construction of load bearing walls. It was observed;a significant improvement of the reinforced blocks under flexure than under compression.