Hydrogen adsorption characteristics of woodceramics,made from radiata pine wood fiber boards carbonized at 1 473 K after impregnation with phenolic resin,with and without chemical treatment in an alkaline(KOH) or an a...Hydrogen adsorption characteristics of woodceramics,made from radiata pine wood fiber boards carbonized at 1 473 K after impregnation with phenolic resin,with and without chemical treatment in an alkaline(KOH) or an acid(H 2 SO 4) solution were investigated The hydrogen adsorption capacity is improved by chemical treatment.The chemical treatment by KOH improves the adsorption capacity more than by H 2 SO 4.The improvement of the capacity level,in any solution,is dependent on the type of chemical in the solution and its concentration.The maximum hydrogen capacity measured at 93 K is mass fraction about w(H) = 2% for the woodceramics after chemical treatment in a volume fraction = 50% KOH solution,although that is about w(H) = 0.7% for one without chemical treatment.The microscopic condition of pores in the woodceramics is thought to vary after chemical treatment.展开更多
文摘Hydrogen adsorption characteristics of woodceramics,made from radiata pine wood fiber boards carbonized at 1 473 K after impregnation with phenolic resin,with and without chemical treatment in an alkaline(KOH) or an acid(H 2 SO 4) solution were investigated The hydrogen adsorption capacity is improved by chemical treatment.The chemical treatment by KOH improves the adsorption capacity more than by H 2 SO 4.The improvement of the capacity level,in any solution,is dependent on the type of chemical in the solution and its concentration.The maximum hydrogen capacity measured at 93 K is mass fraction about w(H) = 2% for the woodceramics after chemical treatment in a volume fraction = 50% KOH solution,although that is about w(H) = 0.7% for one without chemical treatment.The microscopic condition of pores in the woodceramics is thought to vary after chemical treatment.