The high water-cement ratio concrete specimens under biaxial compression that completed in a triaxial testing machine were experimentally studied. Strength and deformations of plain concrete specimens in two loading d...The high water-cement ratio concrete specimens under biaxial compression that completed in a triaxial testing machine were experimentally studied. Strength and deformations of plain concrete specimens in two loading direction under biaxial compression with stress ratio of a=0, 0.25, 0.5, 0.75, 1.0 were obtained after 0, 25, 50 cycles of freeze-thaw. Influences of freeze-thaw cycles and stress ratio on the peak stress and deformation of this point were analyzed according to the experimental results, Based on the test data, the failure criterion expressed in terms of principal stress after different cycles of freeze-thaw, and the failure criterion with consideration of the influence of freeze-thaw cycle and stress ratio were proposed respectively.展开更多
基金the National Natural Science Foundation of China(No.50479059)National Basic Research Program(No.2007CB714202)
文摘The high water-cement ratio concrete specimens under biaxial compression that completed in a triaxial testing machine were experimentally studied. Strength and deformations of plain concrete specimens in two loading direction under biaxial compression with stress ratio of a=0, 0.25, 0.5, 0.75, 1.0 were obtained after 0, 25, 50 cycles of freeze-thaw. Influences of freeze-thaw cycles and stress ratio on the peak stress and deformation of this point were analyzed according to the experimental results, Based on the test data, the failure criterion expressed in terms of principal stress after different cycles of freeze-thaw, and the failure criterion with consideration of the influence of freeze-thaw cycle and stress ratio were proposed respectively.