In this study the partially divorced eutectic microstructure ofα-Mg andβ-Mg17Al12was investigated by electron backscatter diffraction,transmission electron microscopy,and phase-field modeling in hypoeutectic Mg-Al a...In this study the partially divorced eutectic microstructure ofα-Mg andβ-Mg17Al12was investigated by electron backscatter diffraction,transmission electron microscopy,and phase-field modeling in hypoeutectic Mg-Al alloys.The orientation relationships between the individual eutecticαgrains,eutecticβphase,and primaryαgrains were investigated.While the amount of eutectic morphology is primarily determined by the Al content,the in-depth microstructure analyses and the phase-field simulation suggest non-interactive nucleation and growth of eutecticαphase in theβphase grown on the interdendritic primaryαdendrites.Also,phase-field simulations showed a preferred nucleation sequence where theβphase nucleates first and subsequently triggers the nucleation of eutecticαphase at the movingβphase solidification front,which supports the microstructural analysis results.展开更多
基金supported by the Fundamental Research Program of Korea Institute of Materials Science(PNK7760 and PNK7770)the National Research Foundation of Korea(2020R1A2C2008416 and 2021M3H4A6A01049712)。
文摘In this study the partially divorced eutectic microstructure ofα-Mg andβ-Mg17Al12was investigated by electron backscatter diffraction,transmission electron microscopy,and phase-field modeling in hypoeutectic Mg-Al alloys.The orientation relationships between the individual eutecticαgrains,eutecticβphase,and primaryαgrains were investigated.While the amount of eutectic morphology is primarily determined by the Al content,the in-depth microstructure analyses and the phase-field simulation suggest non-interactive nucleation and growth of eutecticαphase in theβphase grown on the interdendritic primaryαdendrites.Also,phase-field simulations showed a preferred nucleation sequence where theβphase nucleates first and subsequently triggers the nucleation of eutecticαphase at the movingβphase solidification front,which supports the microstructural analysis results.