SnO2 and Sb-doped SnO2 particles were synthesized using the polymeric precursor method with different Sn salt precursors： SnCl2.2H2O, SnCl4.5H20, or Sn citrate. Sb2O3 was used as the precursor of Sb, and the molar ra...SnO2 and Sb-doped SnO2 particles were synthesized using the polymeric precursor method with different Sn salt precursors： SnCl2.2H2O, SnCl4.5H20, or Sn citrate. Sb2O3 was used as the precursor of Sb, and the molar ratio of nsn：nsb was held constant. FTIR and TGA/DTA were used to examine the influence of the Sn precursor on the formation and thermal decomposition of the Sn and Sn-Sb complexes. The calcination products obtained from heating the Sn and Sn-Sb complexes at 500℃ in air were analyzed using XRD and TEM analysis. The results revealed that the SnO2 and Sb-doped SnO2 formation temperatures depended on the nature of the Sn precursor. The calcination products were found to be SnO2 and Sb-doped SnO2 particles, which crystallized in a tetragonal cassiterite structure with a highly preferred （110） planar orientation. The Sn precursor and the presence of Sb in the SnO2 matrix strongly influenced the crystallinity and lattice parameters.展开更多
文摘SnO2 and Sb-doped SnO2 particles were synthesized using the polymeric precursor method with different Sn salt precursors： SnCl2.2H2O, SnCl4.5H20, or Sn citrate. Sb2O3 was used as the precursor of Sb, and the molar ratio of nsn：nsb was held constant. FTIR and TGA/DTA were used to examine the influence of the Sn precursor on the formation and thermal decomposition of the Sn and Sn-Sb complexes. The calcination products obtained from heating the Sn and Sn-Sb complexes at 500℃ in air were analyzed using XRD and TEM analysis. The results revealed that the SnO2 and Sb-doped SnO2 formation temperatures depended on the nature of the Sn precursor. The calcination products were found to be SnO2 and Sb-doped SnO2 particles, which crystallized in a tetragonal cassiterite structure with a highly preferred （110） planar orientation. The Sn precursor and the presence of Sb in the SnO2 matrix strongly influenced the crystallinity and lattice parameters.