The fuzzy numerical value analysis method is adopted for the first time, which solves the problem of nanometer electro-thermal in filming process, The key technique is embodied by controlling the time distribution, te...The fuzzy numerical value analysis method is adopted for the first time, which solves the problem of nanometer electro-thermal in filming process, The key technique is embodied by controlling the time distribution, temperature and press in the filming process. The concrete technique of filming is showed by establishing the fuzzy mumbership function of above three indexes, which improves the precision of the materials of nanometer electro-thermal in hot-working. At the same time, the principles of the fuzzy relationship mapping inversion （FRMI） is put forward, Therefore, the standardization and continuity can be met.展开更多
TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase ...TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase arised closest to Ti base at 1173K and 1573K respectively. The phase structure of TiAl/ and the phase structure of TiAlwere observed be- tween AiAl and TC4 under respetive bonding temperature.The fiacture at tensile testing occurred in the bond - line, producing very flat fracture surfaces with some pull-out of the TiAl materials.The ultimate tensile strengths of the joint were approximate to γ-TiAl base marterial.展开更多
文摘The fuzzy numerical value analysis method is adopted for the first time, which solves the problem of nanometer electro-thermal in filming process, The key technique is embodied by controlling the time distribution, temperature and press in the filming process. The concrete technique of filming is showed by establishing the fuzzy mumbership function of above three indexes, which improves the precision of the materials of nanometer electro-thermal in hot-working. At the same time, the principles of the fuzzy relationship mapping inversion （FRMI） is put forward, Therefore, the standardization and continuity can be met.
文摘TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase arised closest to Ti base at 1173K and 1573K respectively. The phase structure of TiAl/ and the phase structure of TiAlwere observed be- tween AiAl and TC4 under respetive bonding temperature.The fiacture at tensile testing occurred in the bond - line, producing very flat fracture surfaces with some pull-out of the TiAl materials.The ultimate tensile strengths of the joint were approximate to γ-TiAl base marterial.