Titaninm-nanohydroxyapatite (Ti-nHA) composite powders, composed of titanium with 10 vol.% and 20 vol.% of nano-hydroxyapatite, were milled in a planetary ball mill using alcohol media to avoid excessive heat. XRD a...Titaninm-nanohydroxyapatite (Ti-nHA) composite powders, composed of titanium with 10 vol.% and 20 vol.% of nano-hydroxyapatite, were milled in a planetary ball mill using alcohol media to avoid excessive heat. XRD and SEM were performed for characterization of the microstructure, and the homogeneity of Ti/HA nanocomposite powder was evaluated by EPMA with prolonged ball milling time. The results show that under the condition of wet milling, the grain size of Ti-nHA composite powders is decreased with the increase in ball milling time and the amount of the addition of nHA. While for milling of 30 h, the nanocomposite powder with free structure, which consists of the nano-hydroxyapatite (nHA) particles and titanium (Ti) phase, is obtained. Three stages of milling can be observed from the dement mapping of Ti, Ca, and P by EPMA; meanwhile, it is found that the nHA would be more homogenously distributed after milling for 30 h.展开更多
基金This work was financially supported by the Science and Technology Key Project of Guangdong Province, China (No.2006B35801001)
文摘Titaninm-nanohydroxyapatite (Ti-nHA) composite powders, composed of titanium with 10 vol.% and 20 vol.% of nano-hydroxyapatite, were milled in a planetary ball mill using alcohol media to avoid excessive heat. XRD and SEM were performed for characterization of the microstructure, and the homogeneity of Ti/HA nanocomposite powder was evaluated by EPMA with prolonged ball milling time. The results show that under the condition of wet milling, the grain size of Ti-nHA composite powders is decreased with the increase in ball milling time and the amount of the addition of nHA. While for milling of 30 h, the nanocomposite powder with free structure, which consists of the nano-hydroxyapatite (nHA) particles and titanium (Ti) phase, is obtained. Three stages of milling can be observed from the dement mapping of Ti, Ca, and P by EPMA; meanwhile, it is found that the nHA would be more homogenously distributed after milling for 30 h.