Reaction behaviors of Pb and Zn sulfates during reduction roasting of Zn leaching residue and flotation of artificial sulfide minerals

To evaluate the feasibility of recovering Pb and Zn sulfides and Ag-containing minerals from Zn leaching residue by the process of reduction roasting followed by flotation,the reaction behaviors of Pb and Zn sulfates during this process were investigated.Chemical analysis showed that the transformation ratios of PbSO4 and ZnSO4 could reach 65.51%and 52.12%,respectively,after reduction roasting,and the introduction of a sulfidation agent could improve the transformation ratios of these sulfates.scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS)revealed that temperature obviously affects the particle size,crystal growth,and morphology of the artificial Pb and Zn sulfide minerals.Particle size analysis demonstrated that the particle size of the materials increases after roasting.Flotation tests revealed that a flotation concentrate composed of 12.01wt%Pb,27.78wt%Zn,and 6.975×10^(−2)wt%Ag with recoveries of 60.54%,29.24%,and 57.64%,respectively,could be obtained after roasting.

Interaction mechanism of ferrate(Ⅵ) with arsenopyrite surface and its effect on flotation separation of chalcopyrite from arsenopyrite

Potassium ferrate(K_(2)FeO_(4)) was used as a novel environmental-friendly depressant,and its inhibition effect on flotation performance of arsenopyrite and chalcopyrite using potassium ethyl xanthate(PEX)as a collector was investigated by flotation experiments,contact angle measurements,adsorption measurements,localized electrochemical impedance spectroscopy(LEIS)measurements,and X-ray photoelectron spectroscopy(XPS)analyses.The results showed that K_(2)FeO_(4)strongly depressed arsenopyrite in a pH range of 4−11,and the flotation separation of chalcopyrite from arsenopyrite could be realized in the presence of 5×10^(−4)mol/L K_(2)FeO_(4)and 5×10^(−5)mol/L PEX at pH 8 or 10.In the presence of K_(2)FeO_(4) and PEX,the contact angle and the xanthate adsorption capacity of arsenopyrite decreased significantly.LEIS measurements showed that the addition of ferrate could significantly increase the impedance of the arsenopyrite surface.XPS analyses further confirmed that ferrate accelerated the oxidation of arsenopyrite surface.