Transmission electron microscopy(TEM)and atom probe tomography(APT)techniques were used to investigate the nanoscale orderedα_(2)(Ti_(3)Al)precipitates in Ti–Al binary alloys.Ti–6Al and Ti–8Al binary alloys were s...Transmission electron microscopy(TEM)and atom probe tomography(APT)techniques were used to investigate the nanoscale orderedα_(2)(Ti_(3)Al)precipitates in Ti–Al binary alloys.Ti–6Al and Ti–8Al binary alloys were solution treated and aged to obtain Widmanstatten microstructure and promoteα_(2)precipitates.The TEM results displayed strong short-range ordering ofα_(2)precipitates in Ti–8Al alloy,while no evidence of the superlattice reflections ofα_(2)in Ti–6Al alloy.The results acquired from APT showed theα_(2)clusters and atoms distribution at the interface between the matrix andα_(2)precipitates.The size and morphology ofα_(2)particles in Ti–8Al alloy,respectively,obtained by TEM and APT are closely consistent.Meanwhile,the APT results displayed tiny size clusters in Ti–6Al alloy,which supposed to give evidence of the initial ordering process ofα_(2)precipitates in the absence of correlative results from TEM.展开更多
基金financially supported by the Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDA22010101)the Natural Key Research and Development Program of China(Nos.2016YFC0304201 and 2016YFC0304206)+1 种基金the Natural Science Foundation of China(No.51871225)the Youth Innovation Promotion Association CAS and Liaoning Revitalization Talents Program(No.XLYC1907005)。
文摘Transmission electron microscopy(TEM)and atom probe tomography(APT)techniques were used to investigate the nanoscale orderedα_(2)(Ti_(3)Al)precipitates in Ti–Al binary alloys.Ti–6Al and Ti–8Al binary alloys were solution treated and aged to obtain Widmanstatten microstructure and promoteα_(2)precipitates.The TEM results displayed strong short-range ordering ofα_(2)precipitates in Ti–8Al alloy,while no evidence of the superlattice reflections ofα_(2)in Ti–6Al alloy.The results acquired from APT showed theα_(2)clusters and atoms distribution at the interface between the matrix andα_(2)precipitates.The size and morphology ofα_(2)particles in Ti–8Al alloy,respectively,obtained by TEM and APT are closely consistent.Meanwhile,the APT results displayed tiny size clusters in Ti–6Al alloy,which supposed to give evidence of the initial ordering process ofα_(2)precipitates in the absence of correlative results from TEM.