A novel Mg-Al LDH film was in-situ prepared hydrothermally in an alkaline aqueous solution on an Al-alloyed AZ31 substrate.The structural,chemical and functional characteristics of the film were explored by means of s...A novel Mg-Al LDH film was in-situ prepared hydrothermally in an alkaline aqueous solution on an Al-alloyed AZ31 substrate.The structural,chemical and functional characteristics of the film were explored by means of scanning electron microscope(SEM),X-ray diffraction(XRD),energy dispersive spectrometer(EDS),polarization curve,AC impedance and salt immersion tests,respectively.The anti-corrosion results indicated that the Mg-Al LDH film on the Al-alloyed AZ31 surface could effectively protect the AZ31 from corrosion attack even after 90 days of immersion in 3.5 wt.%NaCl solution.The protection performance is surprisingly better than most of the reported coatings on Mg alloys.More interestingly,when the Mg-Al LDH film was scratched,the exposed Al-alloyed surface might gradually release metal ions and re-generate dense LDH nano-sheets in the corrosive environment to inhibit the further corrosion there,exhibiting a self-repairing behavior.The combination of the benign long-term protection and desirable self-repairing performance in this new process of surface-alloying and LDH-formation may significantly extend the practical application of magnesium alloys.展开更多
The high-current pulsed electron beam(HCPEB) treatment with current density 6 J/cm^2 was applied on AZ91 Mg alloy to improve its corrosion resistance. Results showed that the net-like Mg_(17)Al_(12) disappeared on the...The high-current pulsed electron beam(HCPEB) treatment with current density 6 J/cm^2 was applied on AZ91 Mg alloy to improve its corrosion resistance. Results showed that the net-like Mg_(17)Al_(12) disappeared on the surface of AZ91 Mg alloy after irradiation by HCPEB, which was instead of supersaturated Al element on the surface. Nevertheless, the application of HCPEB also led to the formation of crater-like and groove-like structures as well as micro-cracks on the surface of AZ91 Mg alloy. After HCPEB treatment by 3, 5 and 10 pulses, the AZ91 Mg alloy exhibited better corrosion resistance.However, the increasing amount of micro-cracks reduced the anti-corrosive properties of AZ91 Mg alloy as the pulse increased to 20 and 30.展开更多
基金The research is supported by the National Science Foundation of China(key project grant No.51731008 and general project grant No.51671163).
文摘A novel Mg-Al LDH film was in-situ prepared hydrothermally in an alkaline aqueous solution on an Al-alloyed AZ31 substrate.The structural,chemical and functional characteristics of the film were explored by means of scanning electron microscope(SEM),X-ray diffraction(XRD),energy dispersive spectrometer(EDS),polarization curve,AC impedance and salt immersion tests,respectively.The anti-corrosion results indicated that the Mg-Al LDH film on the Al-alloyed AZ31 surface could effectively protect the AZ31 from corrosion attack even after 90 days of immersion in 3.5 wt.%NaCl solution.The protection performance is surprisingly better than most of the reported coatings on Mg alloys.More interestingly,when the Mg-Al LDH film was scratched,the exposed Al-alloyed surface might gradually release metal ions and re-generate dense LDH nano-sheets in the corrosive environment to inhibit the further corrosion there,exhibiting a self-repairing behavior.The combination of the benign long-term protection and desirable self-repairing performance in this new process of surface-alloying and LDH-formation may significantly extend the practical application of magnesium alloys.
基金the finacial support from the National Natural Science Foundation of China(Nos.51771128 and 51771129)the Projects of International Cooperation in Shanxi(No.201703D421039)the Natural Science Foundation of Shanxi(No.201601D011034)
文摘The high-current pulsed electron beam(HCPEB) treatment with current density 6 J/cm^2 was applied on AZ91 Mg alloy to improve its corrosion resistance. Results showed that the net-like Mg_(17)Al_(12) disappeared on the surface of AZ91 Mg alloy after irradiation by HCPEB, which was instead of supersaturated Al element on the surface. Nevertheless, the application of HCPEB also led to the formation of crater-like and groove-like structures as well as micro-cracks on the surface of AZ91 Mg alloy. After HCPEB treatment by 3, 5 and 10 pulses, the AZ91 Mg alloy exhibited better corrosion resistance.However, the increasing amount of micro-cracks reduced the anti-corrosive properties of AZ91 Mg alloy as the pulse increased to 20 and 30.