The evolution of the microstructure,microchemistry and magnetic properties of the Sm(CobalFe_(0.28)-CuyZrx)_(7.6)magnets with different Zr and Cu contents was investigated.It is found that the coercivity of the Sm(Co,...The evolution of the microstructure,microchemistry and magnetic properties of the Sm(CobalFe_(0.28)-CuyZrx)_(7.6)magnets with different Zr and Cu contents was investigated.It is found that the coercivity of the Sm(Co,Fe,Cu,Zr)_(z)magnets is sensitive to Zr content.The deficiency of Zr content causes heterogeneity of Cu and Fe distributions,while an excessive Zr content leads to the formation of a SmCoZr impurity phase.The cellular structure and distribution of Cu concentration.gradient between the cell boundary phase and cell pha se are destroyed by inappropriate Zr content,which results in a reduction of coercivity.The Cu concentration difference between the cell boundary phase and cell phase increases with increasing Cu content.The coercivity of the Sm(CobalFe_(0.28)CuyZ_(r0.02))_(7.6)magnets increases from 10.4 to 25.4 kOe for y=0.05 and y=0.07.However,the excess of Cu element destroys the cell boundary phase and enlarges the cell size,resulting in a significant decrease of squareness and energy density.The optimum performance(remanence of 11.4 kG,coercivity of 25.4 kOe,maximum magnetic ene rgy product of 30.4 MGOe)was obtained for the Sm(Co_(0.63)Fe_(0.28)Cu_(0.07)Zr_(0.02))_(7.6)magnet.展开更多
基金the National Natural Science Foundation of China(51871005,51931007)the International S&T Cooperation Program of China(2015DFG52020)。
文摘The evolution of the microstructure,microchemistry and magnetic properties of the Sm(CobalFe_(0.28)-CuyZrx)_(7.6)magnets with different Zr and Cu contents was investigated.It is found that the coercivity of the Sm(Co,Fe,Cu,Zr)_(z)magnets is sensitive to Zr content.The deficiency of Zr content causes heterogeneity of Cu and Fe distributions,while an excessive Zr content leads to the formation of a SmCoZr impurity phase.The cellular structure and distribution of Cu concentration.gradient between the cell boundary phase and cell pha se are destroyed by inappropriate Zr content,which results in a reduction of coercivity.The Cu concentration difference between the cell boundary phase and cell phase increases with increasing Cu content.The coercivity of the Sm(CobalFe_(0.28)CuyZ_(r0.02))_(7.6)magnets increases from 10.4 to 25.4 kOe for y=0.05 and y=0.07.However,the excess of Cu element destroys the cell boundary phase and enlarges the cell size,resulting in a significant decrease of squareness and energy density.The optimum performance(remanence of 11.4 kG,coercivity of 25.4 kOe,maximum magnetic ene rgy product of 30.4 MGOe)was obtained for the Sm(Co_(0.63)Fe_(0.28)Cu_(0.07)Zr_(0.02))_(7.6)magnet.