Porous bowl-shaped VS2 nanosheets/graphene composite for high-rate lithium-ion storage

Two-dimensional (2D) layered vanadium disulfide (VS2) is a promising anode material for lithium ion batteries (LIBs) due to the high theoretical capacity.However,it remains a challenge to synthesize monodispersed ultrathin VS2 nanosheets to realize the full potential.Herein,a novel solvothermal method has been developed to prepare the monodispersed bowl-shaped NH3-inserted VS2 nanosheets (VS2).The formation of such a unique structure is caused by the blocked growth of (001) or (002) crystal planes in combination with a ripening process driven by the thermodynamics.The annealing treatment in Ar/H2creates porous monodispersed VS2(H-VS2),which is subsequently integrated with graphene oxide to form porous monodispersed H-VS2/rGO composite coupled with a reduction process.As an anode material for LIBs,H-VS2/rGO delivers superior rate performance and longer cycle stability:a high average capacity of 868/525 mAh g^-1 at a current density of 1/10 A g^-1;a reversible capacity of 1177/889 mAh g^-1 after 150/500 cycles at 0.2/1 A g^-1.Such excellent electrochemical performance may be attributed to the increased active sites available for lithium storage,the alleviated volume variations and the shortened Li-ion diffusion induced from the porous structure with large specific surface area,as well as the protective effect from graphene nanosheets.

Electrospun Sb2Se3@C nanofibers with excellent lithium storage properties

Antimony-based materials have become promising anodes within lithium-ion batteries(LIBs)due to their low cost and the high theoretical capacity.However,there is a potential to further enhance the electrochemical performance of such antimony-based materials.Herein,Sb2Se3@C nanofibers(Sb2Se3@CNFs)are designed and obtained via a novel electrospinning method.Upon electrochemically testing as an anode within LIBs,the Sb2Se3@CNFs(annealed at 600℃)delivers a remarkably good cycling performance of 625 mAh/g at 100 mA/g after 100 cycles.Moreover,it still remains at 490 mAh/g after 500 cycles with an applied current density of 1.0 A/g.The excellent performance of the Sb2 Se3@CNFs can be attributed to the fact that the N-doped C matrices not only remit the volume expansion of materials,but also enhance the electrical and ionic conductivity thusly increasing the lithium-ion diffusion.The obtained Sb2Se3@CNFs are promising anode for LIBs in the future.