Plate-like single-crystalline BaBi_(4)Ti_(4)O_(15) particles were synthesized by the molten salt synthesis(MSS)method.The effects of sintering temperature,holding time,and NaCl-KCl molten salt content on the phase str...Plate-like single-crystalline BaBi_(4)Ti_(4)O_(15) particles were synthesized by the molten salt synthesis(MSS)method.The effects of sintering temperature,holding time,and NaCl-KCl molten salt content on the phase structure and morphology of plate-like BaBi_(4)-Ti_(4)O_(15) particles were investigated.The results show that plate-like BaBi_(4)Ti_(4)O_(15) particles can be synthesized when the sintering temperature is above 800°C.The size of particles increases with increasing sintering temperature and molten salt content.Largely anisotropic plate-like BaBi_(4)Ti_(4)O_(15) particles with diameter≥10μm and thickness of~0.3μm can be obtained under the optimum process parameters.The crystal structure of BaBi_(4)Ti_(4)O_(15) was determined as A21am by TEM,which should be attributed to the Bi3+and Ba2+diffusing into[TiO6]octahedrons.展开更多
Transparent ceramics are at the heart of modern magneto-optical materials providing promising opportunities for Faraday isolators.1.0 at%RE:Tb3Ga5O12(rare earth(RE)=Pr,Tm,Dy)transparent ceramics were successfully prep...Transparent ceramics are at the heart of modern magneto-optical materials providing promising opportunities for Faraday isolators.1.0 at%RE:Tb3Ga5O12(rare earth(RE)=Pr,Tm,Dy)transparent ceramics were successfully prepared by air sintering and sequential HIP technique using the coprecipitated powders as the raw material.All the powders have shown to be a pure cubic terbium gallium garnet(TGG)phase and exhibit good dispersion.Additionally,a change could not be observed in particle shape with the different doped ions.After the two-step sintering,all the obtained ceramics have good optical quality,and the in-line transmittances at 1070 nm are higher than 80%.Moreover,no secondary phase can be detected from the microstructures.However,the pores which remain entrapped in the ceramics can be noted.The Verdet constant of ceramic samples is optimized by RE doping,and the Verdet constant at 632.8 nm is about−143 rad·T^(−1)·m^(−1),which is about 5%higher than that of TGG ceramics.Finally,the thermo-optical properties of 1.0 at%RE:TGG transparent ceramics are compared.The annealed TGG ceramic showed the best thermo-optical properties,and the thermally induced depolarization of 1.0 at%Ce:TGG and 1.0 at%Tm:TGG was inferior to that of annealed TGG ceramic.展开更多
Fine grained 8 mol%yttria-stabilized zirconia(8YSZ)transparent ceramics with high optical and mechanical properties were fabricated by air pre-sintering and hot isostatic pressing(HIP)using commercial 8YSZ powders as ...Fine grained 8 mol%yttria-stabilized zirconia(8YSZ)transparent ceramics with high optical and mechanical properties were fabricated by air pre-sintering and hot isostatic pressing(HIP)using commercial 8YSZ powders as the raw material.The pre-sintered ceramics with fine grains and appropriate relative density play a key role to achieve high transparency and suppressed grain size after HIP post-treatment at relatively low temperatures.With the increase of HIP temperature from 1350 to 1550℃,the in-line transmittance of 8YSZ ceramics at 600 nm increases from 56.9%to 71.5%(2.5 mm in thickness),and the average grain size increases from 2.4 to 16.3μm.The corresponding bending strength of 8YSZ transparent ceramics decreases from 328±20 to 289±19 MPa,the hardness(H)decreases from 12.9±0.1 to 12.5±0.2 GPa,and the fracture toughness(KIC)decreases from 1.30±0.02 to 1.26±0.03 MPa·m^(1/2).Systematical investigations were carried out to study the combination of high optical transparency and excellent mechanical properties in 8YSZ ceramics.展开更多
基金supported by the China-Poland International Collaboration Fund of National Natural Science Foundation of China(51961135301)the National Natural Science Foundation of China(12074318 and 52072301)+1 种基金the International Cooperation Foundation of Shaanxi Province(2022KW-34)the Undergraduate Innovation and Entrepreneurship Training Program of Shaanxi Province(S202210699511)and the‘111’Project(B20028).
文摘Plate-like single-crystalline BaBi_(4)Ti_(4)O_(15) particles were synthesized by the molten salt synthesis(MSS)method.The effects of sintering temperature,holding time,and NaCl-KCl molten salt content on the phase structure and morphology of plate-like BaBi_(4)-Ti_(4)O_(15) particles were investigated.The results show that plate-like BaBi_(4)Ti_(4)O_(15) particles can be synthesized when the sintering temperature is above 800°C.The size of particles increases with increasing sintering temperature and molten salt content.Largely anisotropic plate-like BaBi_(4)Ti_(4)O_(15) particles with diameter≥10μm and thickness of~0.3μm can be obtained under the optimum process parameters.The crystal structure of BaBi_(4)Ti_(4)O_(15) was determined as A21am by TEM,which should be attributed to the Bi3+and Ba2+diffusing into[TiO6]octahedrons.
基金supported by the National Key R&D Program of China(Grant No.2017YFB0310500)the NSFC-RFBR Cooperative Research Project(Grant No.61911530135)+1 种基金the Key Research Project of the Frontier Science of the Chinese Academy of Sciences(No.QYZDB-SSW-JSC022)supported partially by the Ministry of High Education and Science of the Russian Federation and the State Task executed in the Institute of Applied Physics RAS(Project No.00352019-0015)。
文摘Transparent ceramics are at the heart of modern magneto-optical materials providing promising opportunities for Faraday isolators.1.0 at%RE:Tb3Ga5O12(rare earth(RE)=Pr,Tm,Dy)transparent ceramics were successfully prepared by air sintering and sequential HIP technique using the coprecipitated powders as the raw material.All the powders have shown to be a pure cubic terbium gallium garnet(TGG)phase and exhibit good dispersion.Additionally,a change could not be observed in particle shape with the different doped ions.After the two-step sintering,all the obtained ceramics have good optical quality,and the in-line transmittances at 1070 nm are higher than 80%.Moreover,no secondary phase can be detected from the microstructures.However,the pores which remain entrapped in the ceramics can be noted.The Verdet constant of ceramic samples is optimized by RE doping,and the Verdet constant at 632.8 nm is about−143 rad·T^(−1)·m^(−1),which is about 5%higher than that of TGG ceramics.Finally,the thermo-optical properties of 1.0 at%RE:TGG transparent ceramics are compared.The annealed TGG ceramic showed the best thermo-optical properties,and the thermally induced depolarization of 1.0 at%Ce:TGG and 1.0 at%Tm:TGG was inferior to that of annealed TGG ceramic.
基金This work was supported by the National Key R&D Program of China(Grant No.2021YFE0104800)the Key Research Project of Frontier Science of Chinese Academy of Sciences(Grant No.QYZDB-SSW-JSC022).
文摘Fine grained 8 mol%yttria-stabilized zirconia(8YSZ)transparent ceramics with high optical and mechanical properties were fabricated by air pre-sintering and hot isostatic pressing(HIP)using commercial 8YSZ powders as the raw material.The pre-sintered ceramics with fine grains and appropriate relative density play a key role to achieve high transparency and suppressed grain size after HIP post-treatment at relatively low temperatures.With the increase of HIP temperature from 1350 to 1550℃,the in-line transmittance of 8YSZ ceramics at 600 nm increases from 56.9%to 71.5%(2.5 mm in thickness),and the average grain size increases from 2.4 to 16.3μm.The corresponding bending strength of 8YSZ transparent ceramics decreases from 328±20 to 289±19 MPa,the hardness(H)decreases from 12.9±0.1 to 12.5±0.2 GPa,and the fracture toughness(KIC)decreases from 1.30±0.02 to 1.26±0.03 MPa·m^(1/2).Systematical investigations were carried out to study the combination of high optical transparency and excellent mechanical properties in 8YSZ ceramics.