Microbiologically influenced corrosion(MIC) is a big threat to the strength and safety of many metallic materials used in different environments throughout the world. The metabolites and bioactivity of the microorgani...Microbiologically influenced corrosion(MIC) is a big threat to the strength and safety of many metallic materials used in different environments throughout the world. The metabolites and bioactivity of the microorganisms cause severe deterioration on the metals. In this study, MIC of pure titanium(Ti) was studied in the presence of a highly corrosive aerobic marine bacterium Pseudomonas aeruginosa. The results obtained from electrochemical test showed that Ti was corrosion resistant in the abiotic culture medium after 14 d, while the increased corrosion current density(i_(corr)) obtained from polarization curves and the decreased charge transfer resistance(R_(ct)) from electrochemical impedance spectroscopy(EIS)indicated the accelerated corrosion of Ti caused by P. aeruginosa biofilm. For further confirmation of the above results, the surface of Ti was investigated using scanning electron microscopy(SEM), confocal laser scanning microscopy(CLSM) and X-ray photoelectron spectroscopy(XPS). According to the XPS results, TiO_2 was formed in both abiotic and biotic conditions, while unstable oxide Ti_2O_3 was detected in the presence of P. aeruginosa, leading to the defects in the passive film and localized corrosion. Pitting corrosion was investigated with the help of CLSM, and the largest pit depth found on Ti surface immersed in P. aeruginosa was 1.2 μm. Ti was not immune to MIC caused by P. aeruginosa.展开更多
基金supportedfinancially by the National Natural Science Foundation of China(No.U1660118)the National Basic Research Program of China(No.2014CB643300)the National Environmental Corrosion Platform(NECP)
文摘Microbiologically influenced corrosion(MIC) is a big threat to the strength and safety of many metallic materials used in different environments throughout the world. The metabolites and bioactivity of the microorganisms cause severe deterioration on the metals. In this study, MIC of pure titanium(Ti) was studied in the presence of a highly corrosive aerobic marine bacterium Pseudomonas aeruginosa. The results obtained from electrochemical test showed that Ti was corrosion resistant in the abiotic culture medium after 14 d, while the increased corrosion current density(i_(corr)) obtained from polarization curves and the decreased charge transfer resistance(R_(ct)) from electrochemical impedance spectroscopy(EIS)indicated the accelerated corrosion of Ti caused by P. aeruginosa biofilm. For further confirmation of the above results, the surface of Ti was investigated using scanning electron microscopy(SEM), confocal laser scanning microscopy(CLSM) and X-ray photoelectron spectroscopy(XPS). According to the XPS results, TiO_2 was formed in both abiotic and biotic conditions, while unstable oxide Ti_2O_3 was detected in the presence of P. aeruginosa, leading to the defects in the passive film and localized corrosion. Pitting corrosion was investigated with the help of CLSM, and the largest pit depth found on Ti surface immersed in P. aeruginosa was 1.2 μm. Ti was not immune to MIC caused by P. aeruginosa.