Acrylonitrile rubber(NBR)composites filled with barium titanate(BT)were prepared using an internal mixer and a two-roll mill.Also,a secondary filler,namely carbon nanotubes(CNT),was added in order to find a potential ...Acrylonitrile rubber(NBR)composites filled with barium titanate(BT)were prepared using an internal mixer and a two-roll mill.Also,a secondary filler,namely carbon nanotubes(CNT),was added in order to find a potential synergistic blend ratio of BT and CNT.The cure characteristics,tensile and dielectric properties(dielectric constant and dielectric loss)of the composites were determined.It was found that NBR/BT composites with CNT secondary filler,at a proper BT:CNT ratio,exhibited shorter scorch time(ts1)and cure time(tc90)together with superior tensile properties and reinforcement efficiency,relative to the one with only the primary filler.In addition,the NBR/BT-CNT composite with 80 phr BT and 1–2 phr CNT had dielectric constant of 100–500,dielectric loss of 12–100 and electrical conductivity below 10−4 S/m together with high thermal stability.Thus,with a proper BT:CNT mix and filler loading,we can produce mechanically superior rubber composites that are easy to process and low-cost,for flexible dielectric materials application.展开更多
基金by a grant from the government budget of Prince of Songkla University and Natural Rubber Innovation Research Institute(NR-IRI)(No.SIT610284S)the graduate school of Prince of Songkla University and by Prince of Songkla University,Surat Thani Campus。
文摘Acrylonitrile rubber(NBR)composites filled with barium titanate(BT)were prepared using an internal mixer and a two-roll mill.Also,a secondary filler,namely carbon nanotubes(CNT),was added in order to find a potential synergistic blend ratio of BT and CNT.The cure characteristics,tensile and dielectric properties(dielectric constant and dielectric loss)of the composites were determined.It was found that NBR/BT composites with CNT secondary filler,at a proper BT:CNT ratio,exhibited shorter scorch time(ts1)and cure time(tc90)together with superior tensile properties and reinforcement efficiency,relative to the one with only the primary filler.In addition,the NBR/BT-CNT composite with 80 phr BT and 1–2 phr CNT had dielectric constant of 100–500,dielectric loss of 12–100 and electrical conductivity below 10−4 S/m together with high thermal stability.Thus,with a proper BT:CNT mix and filler loading,we can produce mechanically superior rubber composites that are easy to process and low-cost,for flexible dielectric materials application.