Ni-doped ZnO thin films (Ni concentration up to 10 mol%) were generated on Si (100) substrates by a sol-gel technique. The films showed wurtzite structure and no other phase was found. The chemical state of Ni was fou...Ni-doped ZnO thin films (Ni concentration up to 10 mol%) were generated on Si (100) substrates by a sol-gel technique. The films showed wurtzite structure and no other phase was found. The chemical state of Ni was found to be bivalent by X-ray photoelectron spectroscopy. The results of magnetic measurements at room temperature indicated that the films were ferromagnetic, and magnetic moment decreased with rise of Ni concentration. The magnetization of Ni (10 mol%)-doped ZnO film annealed in nitrogen was lower than that annealed in argon, suggesting that the density of defects had an effect on ferromagnetism.展开更多
基金Supported by the National Natural Science Foundation of China (Grant No.10674059)the National Basic Research Program of China (“973” Project) (Grant No.2005CB623605)
文摘Ni-doped ZnO thin films (Ni concentration up to 10 mol%) were generated on Si (100) substrates by a sol-gel technique. The films showed wurtzite structure and no other phase was found. The chemical state of Ni was found to be bivalent by X-ray photoelectron spectroscopy. The results of magnetic measurements at room temperature indicated that the films were ferromagnetic, and magnetic moment decreased with rise of Ni concentration. The magnetization of Ni (10 mol%)-doped ZnO film annealed in nitrogen was lower than that annealed in argon, suggesting that the density of defects had an effect on ferromagnetism.