Acetyl crosslinked polystyrene (EPS) and crosslinked bromoacetyl polystyrene (BEPS)beads were synthesized by Fridel-Crafts acetylation of polystyrene (PS) and bromination of EPS respectively. FTIR, XPS, and TG-TDG wer...Acetyl crosslinked polystyrene (EPS) and crosslinked bromoacetyl polystyrene (BEPS)beads were synthesized by Fridel-Crafts acetylation of polystyrene (PS) and bromination of EPS respectively. FTIR, XPS, and TG-TDG were employed to characterize their structures. The results revealed there are two types of bromine in the BEPS molecule. One is in the main chain of polystyrene and the other is in the acetyl. The results of TG-DTG showed that the rates of loss weight of PS, EPS, and BEPS were 92.7%, 92.2%, and 81.3% among the 300 ℃～500 ℃; 7.3%, 7.8%, and 18. 7% in 594 ℃, 660 ℃, and 584.8 ℃, respectively.展开更多
By the reaction of poly(bromoacetyl styrene) (EBPS) with thiaurea (TU), a kind of novel chelating resin with heterocyaclic ring of sulfur and nitrogen, poly[4-(2-amino)thiazoleyl-4- vinylbenzene], was synthesized. Its...By the reaction of poly(bromoacetyl styrene) (EBPS) with thiaurea (TU), a kind of novel chelating resin with heterocyaclic ring of sulfur and nitrogen, poly[4-(2-amino)thiazoleyl-4- vinylbenzene], was synthesized. Its structure was characterized by FTIR and elemental analysis. The factors which have influence on the reaction such as reaction time, solvents, and molar ratio of reactants were investigated.展开更多
基金National Natural Science Foundation of China (No.29906008) and Nature Science Foundation of Shandong Province (No.Q99B15).
文摘Acetyl crosslinked polystyrene (EPS) and crosslinked bromoacetyl polystyrene (BEPS)beads were synthesized by Fridel-Crafts acetylation of polystyrene (PS) and bromination of EPS respectively. FTIR, XPS, and TG-TDG were employed to characterize their structures. The results revealed there are two types of bromine in the BEPS molecule. One is in the main chain of polystyrene and the other is in the acetyl. The results of TG-DTG showed that the rates of loss weight of PS, EPS, and BEPS were 92.7%, 92.2%, and 81.3% among the 300 ℃～500 ℃; 7.3%, 7.8%, and 18. 7% in 594 ℃, 660 ℃, and 584.8 ℃, respectively.
基金National Natural Science Foundation of China (No.29906008) and Natural Science Foundation of Shandong Province (No.Q99B15)
文摘By the reaction of poly(bromoacetyl styrene) (EBPS) with thiaurea (TU), a kind of novel chelating resin with heterocyaclic ring of sulfur and nitrogen, poly[4-(2-amino)thiazoleyl-4- vinylbenzene], was synthesized. Its structure was characterized by FTIR and elemental analysis. The factors which have influence on the reaction such as reaction time, solvents, and molar ratio of reactants were investigated.