Three-dimensional ordered macroporous (3DOM) La1?xKxNiO3 perovskite-type catalysts were successfully prepared by a colloidal crystal template method and characterized by scanning electron microscopy, transmission elec...Three-dimensional ordered macroporous (3DOM) La1?xKxNiO3 perovskite-type catalysts were successfully prepared by a colloidal crystal template method and characterized by scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, energy-dispersive X-ray scattering elemental mapping, X-ray diffraction, Raman and X-ray photoelectron spectroscopy, and temperature-programmed reduction of H2. Further, their catalytic activity in soot combustion was determined by temperature-programmed oxidation reaction. K substitution into the LaNiO3 lattice led to remarkably improved catalytic activity of this catalyst in soot combustion. Amongst various catalysts, La0.95K0.05NiO3 exhibited the highest activity in soot combustion (with its T50 and CO2 S values being 338 °C and 98.2%, respectively), which is comparable to the catalytic activities of Pt-based catalysts under the condition of poor contact between the soot and the catalyst. K-substitution improves the valence state of Ni and increases the number of oxygen vacancies, thereby leading to increased density of surface-active oxygen species. The active oxygen species play a vital role in catalyzing the elimination of soot. The perovskite-type La1?xKxNiO3 nanocatalysts with 3DOM structure without noble metals have potential for practical applications in the catalytic combustion of diesel soot particles.展开更多
Nanocatalysts consisting of three‐dimensionally ordered macroporous(3DOM)TiO2‐supported ultrafine Pd nanoparticles(Pd/3DOM‐TiO2‐GBMR)were readily fabricated by gas bubbling‐assisted membrane reduction(GBMR)method...Nanocatalysts consisting of three‐dimensionally ordered macroporous(3DOM)TiO2‐supported ultrafine Pd nanoparticles(Pd/3DOM‐TiO2‐GBMR)were readily fabricated by gas bubbling‐assisted membrane reduction(GBMR)method.These catalysts had a well‐defined and highly ordered macroporous nanostructure with an average pore size of 280 nm.In addition,ultrafine hemispherical Pd nanoparticles(NPs)with a mean particle size of 1.1 nm were found to be well dispersed over the surface of the 3DOM‐TiO2 support and deposited on the inner walls of the material.The nanostructure of the 3DOM‐TiO2 support ensured efficient contact between soot particles and the catalyst.The large interface area between the ultrafine Pd NPs and the TiO2 also increased the density of sites for O2 activation as a result of the strong metal(Pd)‐support(TiO2)interaction(SMSI).A Pd/3DOM‐TiO2‐GBMR catalyst with ultrafine Pd NPs(1.1 nm)exhibited higher catalytic activity during diesel soot combustion compared with that obtained from a specimen having relatively large Pd NPs(5.0 nm).The T10,T50 and T90 values obtained from the former were 295,370 and 415°C.Both the activity and nanostructure of the Pd/3DOM‐TiO2‐GBMR catalyst were stable over five replicate soot oxidation trials.These results suggest that nanocatalysts having a 3DOM structure together with ultrafine Pd NPs can decrease the amount of Pd required,and that this approach has potential practical applications in the catalytic combustion of diesel soot particles.展开更多
基金supported by the National Natural Science Foundation of China(21673142)National Engineering Laboratory for Mobile Source Emission Control Technology(NELMS2017A05)+1 种基金PetroChina Innovation Foundation(2018D-5007-0505)Science Foundation of China University of Petroleum,Beijing(242017QNXZ02,2462018BJC005)~~
文摘Three-dimensional ordered macroporous (3DOM) La1?xKxNiO3 perovskite-type catalysts were successfully prepared by a colloidal crystal template method and characterized by scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, energy-dispersive X-ray scattering elemental mapping, X-ray diffraction, Raman and X-ray photoelectron spectroscopy, and temperature-programmed reduction of H2. Further, their catalytic activity in soot combustion was determined by temperature-programmed oxidation reaction. K substitution into the LaNiO3 lattice led to remarkably improved catalytic activity of this catalyst in soot combustion. Amongst various catalysts, La0.95K0.05NiO3 exhibited the highest activity in soot combustion (with its T50 and CO2 S values being 338 °C and 98.2%, respectively), which is comparable to the catalytic activities of Pt-based catalysts under the condition of poor contact between the soot and the catalyst. K-substitution improves the valence state of Ni and increases the number of oxygen vacancies, thereby leading to increased density of surface-active oxygen species. The active oxygen species play a vital role in catalyzing the elimination of soot. The perovskite-type La1?xKxNiO3 nanocatalysts with 3DOM structure without noble metals have potential for practical applications in the catalytic combustion of diesel soot particles.
基金supported by the National Natural Science Foundation of China(21673142,21477164)the National High Technology Research and Development Program of China(863 Program,2015AA030903)~~
文摘Nanocatalysts consisting of three‐dimensionally ordered macroporous(3DOM)TiO2‐supported ultrafine Pd nanoparticles(Pd/3DOM‐TiO2‐GBMR)were readily fabricated by gas bubbling‐assisted membrane reduction(GBMR)method.These catalysts had a well‐defined and highly ordered macroporous nanostructure with an average pore size of 280 nm.In addition,ultrafine hemispherical Pd nanoparticles(NPs)with a mean particle size of 1.1 nm were found to be well dispersed over the surface of the 3DOM‐TiO2 support and deposited on the inner walls of the material.The nanostructure of the 3DOM‐TiO2 support ensured efficient contact between soot particles and the catalyst.The large interface area between the ultrafine Pd NPs and the TiO2 also increased the density of sites for O2 activation as a result of the strong metal(Pd)‐support(TiO2)interaction(SMSI).A Pd/3DOM‐TiO2‐GBMR catalyst with ultrafine Pd NPs(1.1 nm)exhibited higher catalytic activity during diesel soot combustion compared with that obtained from a specimen having relatively large Pd NPs(5.0 nm).The T10,T50 and T90 values obtained from the former were 295,370 and 415°C.Both the activity and nanostructure of the Pd/3DOM‐TiO2‐GBMR catalyst were stable over five replicate soot oxidation trials.These results suggest that nanocatalysts having a 3DOM structure together with ultrafine Pd NPs can decrease the amount of Pd required,and that this approach has potential practical applications in the catalytic combustion of diesel soot particles.