Magnetic expanded graphite(EG)hybrids were synthesized by co-intercalation polymerization of aniline together with transition metal ions.Experimental results show that metal ions(Fe,Co,Ni,Cu)and even their mixtures ca...Magnetic expanded graphite(EG)hybrids were synthesized by co-intercalation polymerization of aniline together with transition metal ions.Experimental results show that metal ions(Fe,Co,Ni,Cu)and even their mixtures can co-intercalate into graphite interlayers with flexibly controllable ratios and contents.Among these co-intercalation compounds,Fe/Ni-intercalated graphite with a predesigned mole ratio of 1:3 transforms into NiFe_(2)O_(4)/FeNi_(3)@EG during the annealing process.The synthesized magnetic EG hybrids present multiband microwave absorption in C and X bands due to improved impedance match as well as significantly enhanced interfacial polarization relaxation induced by multi-componential metals.The reflection values of−39.1 dB at 6.95 GHz and−25.7 dB at 9.4 GHz are achieved with an ultra-low loading of 5 wt.%.This work provides a flexible approach for tuning the components and structures of magnetic EG hybrids,which may contribute to the development of microwave absorption materials with superior performances.展开更多
基金the financial support of the National Natural Science Foundation of China(No.51573149)the Key R&D Projects in Sichuan Province(Nos.2020ZDZX0005 and 2020ZDZX0008).
文摘Magnetic expanded graphite(EG)hybrids were synthesized by co-intercalation polymerization of aniline together with transition metal ions.Experimental results show that metal ions(Fe,Co,Ni,Cu)and even their mixtures can co-intercalate into graphite interlayers with flexibly controllable ratios and contents.Among these co-intercalation compounds,Fe/Ni-intercalated graphite with a predesigned mole ratio of 1:3 transforms into NiFe_(2)O_(4)/FeNi_(3)@EG during the annealing process.The synthesized magnetic EG hybrids present multiband microwave absorption in C and X bands due to improved impedance match as well as significantly enhanced interfacial polarization relaxation induced by multi-componential metals.The reflection values of−39.1 dB at 6.95 GHz and−25.7 dB at 9.4 GHz are achieved with an ultra-low loading of 5 wt.%.This work provides a flexible approach for tuning the components and structures of magnetic EG hybrids,which may contribute to the development of microwave absorption materials with superior performances.