Photocatalytic technology can solve various environmental pollution problems,especially antibiotic pollution.A novel La-doped MIL-53(Al)/ZnO composite material was successfully synthesized by a combination of hydrothe...Photocatalytic technology can solve various environmental pollution problems,especially antibiotic pollution.A novel La-doped MIL-53(Al)/ZnO composite material was successfully synthesized by a combination of hydrothermal method and calcination,showing high photocatalytic degradation percent of sulfamethazine(SMT).The 2 mol%La MIL-53(Al)/ZnO photocatalyst shows the highest degradation efficiency toward SMT(92%)within 120 min,which is 4.1 times higher than pure ZnO(increased from 18%to 92%).In addition,the degradation analysis of SMT by high performance liquid chromatography proves that the products are CO_(2) and H_(2)O.The improved photocatalytic activity is mostly caused by the following factors.(1)Doping La ions can decrease the band gap of ZnO,enhance light response,and effectively enhance the separation rate of photo-generated holes and electrons.(2)MIL-53(Al)can adsorb SMT and promote the separation of electron.This work shows that the synthesized La-doped MIL-53(Al)/ZnO photocatalyst is expected to be used as a green and effective method for treatment of environment water pollution.展开更多
A one-step microwave irradiation method was used to deposit carbon and nitrogen co-doped TiO2((C, N)-TiO2) on commercial brick((C, N)-TiO2/brick). The as-prepared samples were characterized by X-ray diffractio...A one-step microwave irradiation method was used to deposit carbon and nitrogen co-doped TiO2((C, N)-TiO2) on commercial brick((C, N)-TiO2/brick). The as-prepared samples were characterized by X-ray diffraction, ultraviolet–visible(UV–vis) diffuse reflectance spectroscopy, photoluminescence spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy(SEM). A selective technique was also used to investigate the concentration of hydroxyl radicals during UV–vis irradiation of the Methyl Orange solution with the as-prepared samples. The C and N dopants enhanced visible light absorption and provided a longer lifetime for the photo-generated electron–hole pairs. The SEM images showed that the as-prepared sample is porous. The dark adsorption and photodegradation test for(C, N)-TiO2/brick showed good photodegradation and good recyclability. The best photodegradation rate was 94% after 2 hr. The maximum degradation rate was maintained even after the 6th cycle. The good photocatalytic properties are attributed to the enhanced visible light absorption, enhanced pollutant adsorption arising from the porous structure of the(C, N)-TiO2 thin film, and longer lifetime of the photo-generated electron–hole pairs.(C, N)-TiO2/brick should have potential commercial applications in photodegradation processes because of its low cost, good photodegradation, and excellent recyclability.展开更多
基金Project supported by the National Natural Science Foundation of China (11674106)。
文摘Photocatalytic technology can solve various environmental pollution problems,especially antibiotic pollution.A novel La-doped MIL-53(Al)/ZnO composite material was successfully synthesized by a combination of hydrothermal method and calcination,showing high photocatalytic degradation percent of sulfamethazine(SMT).The 2 mol%La MIL-53(Al)/ZnO photocatalyst shows the highest degradation efficiency toward SMT(92%)within 120 min,which is 4.1 times higher than pure ZnO(increased from 18%to 92%).In addition,the degradation analysis of SMT by high performance liquid chromatography proves that the products are CO_(2) and H_(2)O.The improved photocatalytic activity is mostly caused by the following factors.(1)Doping La ions can decrease the band gap of ZnO,enhance light response,and effectively enhance the separation rate of photo-generated holes and electrons.(2)MIL-53(Al)can adsorb SMT and promote the separation of electron.This work shows that the synthesized La-doped MIL-53(Al)/ZnO photocatalyst is expected to be used as a green and effective method for treatment of environment water pollution.
基金supported by the National Natural Science Foundation of China (Nos. 51672090 and 51372092)
文摘A one-step microwave irradiation method was used to deposit carbon and nitrogen co-doped TiO2((C, N)-TiO2) on commercial brick((C, N)-TiO2/brick). The as-prepared samples were characterized by X-ray diffraction, ultraviolet–visible(UV–vis) diffuse reflectance spectroscopy, photoluminescence spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy(SEM). A selective technique was also used to investigate the concentration of hydroxyl radicals during UV–vis irradiation of the Methyl Orange solution with the as-prepared samples. The C and N dopants enhanced visible light absorption and provided a longer lifetime for the photo-generated electron–hole pairs. The SEM images showed that the as-prepared sample is porous. The dark adsorption and photodegradation test for(C, N)-TiO2/brick showed good photodegradation and good recyclability. The best photodegradation rate was 94% after 2 hr. The maximum degradation rate was maintained even after the 6th cycle. The good photocatalytic properties are attributed to the enhanced visible light absorption, enhanced pollutant adsorption arising from the porous structure of the(C, N)-TiO2 thin film, and longer lifetime of the photo-generated electron–hole pairs.(C, N)-TiO2/brick should have potential commercial applications in photodegradation processes because of its low cost, good photodegradation, and excellent recyclability.