The structure of Mo-15.16 Si, Mo-30 Si and Mo-36.3 Si (wt pct) elemental powder mixture during mechanical alloying was studied using electron microscopy and X-ray diffraction. It had been found that, in all the system...The structure of Mo-15.16 Si, Mo-30 Si and Mo-36.3 Si (wt pct) elemental powder mixture during mechanical alloying was studied using electron microscopy and X-ray diffraction. It had been found that, in all the systems under study, silicon disappeared initially during mechanical alloying (MA). In the Mo-Si systems all products were in form of amorphous state after long time milling, but there were different intermediate products. MoSi2 and Mo5Si3 intermetallic compounds in the Mo-30Si and Mo-36.3Si (wt pct) were directly synthesized from elements through inter-diffussion process. The high density of defects and interface of nano-crystal lines induced by ball milling would promote the reaction process. Only in the Mo-15.16Si (wt pct) system was Mo(Si) supersaturated solid solution formed as an intermediate product. Schematic free-energy diagram of Mo-Si system based on the thermodynamics was used to analyze the difference among the intermediate state products.展开更多
文摘The structure of Mo-15.16 Si, Mo-30 Si and Mo-36.3 Si (wt pct) elemental powder mixture during mechanical alloying was studied using electron microscopy and X-ray diffraction. It had been found that, in all the systems under study, silicon disappeared initially during mechanical alloying (MA). In the Mo-Si systems all products were in form of amorphous state after long time milling, but there were different intermediate products. MoSi2 and Mo5Si3 intermetallic compounds in the Mo-30Si and Mo-36.3Si (wt pct) were directly synthesized from elements through inter-diffussion process. The high density of defects and interface of nano-crystal lines induced by ball milling would promote the reaction process. Only in the Mo-15.16Si (wt pct) system was Mo(Si) supersaturated solid solution formed as an intermediate product. Schematic free-energy diagram of Mo-Si system based on the thermodynamics was used to analyze the difference among the intermediate state products.