增材制造Ti6Al4V合金的闪速等离子体电解氧化与在生理介质中的电化学行为

研究激光粉末床熔融增材制造(AM)(又称直接金属激光烧结)技术制备的Ti6Al4V合金等离子体电解氧化(PEO)处理及其电化学行为。通过短时间(<120 s)PEO处理(也称闪速PEO),在AM合金和传统合金表面制备了3~10μm厚、含Ca和P的涂层。然后在改良的α-MEM溶液中,通过动电位极化曲线和电化学阻抗谱(EIS)评估了合金的电化学行为。与传统合金相比,AM合金中形成了细小的层片状α显微组织和层间小尺寸的β相颗粒,这促使了火花的产生,从而促进了PEO涂层的生长。闪速PEO涂层提高了传统合金和AM合金的耐腐蚀性,最薄的涂层(<3μm)提供了高达3倍的保护。AM Ti6Al4V由于其高的晶界密度,易受局部缝隙腐蚀的影响。而即使短至35 s的闪速PEO处理也足以成功避免这种情况。

LDH conversion films for active protection of AZ31 Mg alloy

Zinc aluminium(Zn-Al)and lithium aluminium(Li-Al)–layered double hydroxides(LDH)coatings with incorporated inhibitors(Li-,Mo-and W-based)were successfully synthesized on AZ31 Mg alloy.Zn-Al LDH W and Li-Al LDH Li showed the highest corrosion resistance and were selected for further evaluation.SEM cross-section examination revealed a bi-layer structure composed of an outer part with loose flakes and a denser inner layer.XRD,FTIR,and XPS analysis confirmed the incorporation of the inhibitors.Post-treatments with corrosion inhibitors containing solutions resulted in the selective dissolution of the most external layer of the LDH coating,reducing the surface roughness,hydrophilicity and paint adhesion of the layers.Active corrosion properties were confirmed by SVET evaluation for the Zn-Al LDH W coating.The proposed active corrosion mechanism involves the ion-exchange of aggressive Cl-ions,deposition of hydroxides and competitive adsorption of W-rich corrosion inhibitors.

铝合金高效节能微弧氧化的研究进展（英文）

为增强合金的摩擦腐蚀性能,减小微弧氧化能量损耗,研究了电压控制模式下各种工业用变形、重力铸造和流变铸造铝合金微弧氧化涂层。结果表明:采用传统多孔阳极膜前驱体,减小了微弧氧化能量损耗至50%;添加α-Al2O3粒子的微弧氧化涂层后,6082合金的磨损比电解硬铬的低2倍。通过使用前驱体和疏水后处理,提高了包覆微弧氧化涂层A356合金的长期耐蚀性。