The alkylation of toluene with methanol to selective formation of p-xylene has been systematically studied. ZSM-12 （MTW）/ZSM-5 co-crystalline zeolite in 40：60 proportions have been synthesized by the same molar gel...The alkylation of toluene with methanol to selective formation of p-xylene has been systematically studied. ZSM-12 （MTW）/ZSM-5 co-crystalline zeolite in 40：60 proportions have been synthesized by the same molar gel composition, but at different temperatures and periods than that of ZSM-12 and ZSM-5, separately. All the prepared samples are characterized by XRD, SEM, BET, and XRF. The activity of toluene alkylation was investigated with a mixture of toluene and methanol as a feed over the ZSM-12, ZSM-12/ZSM-5 co-crystalline, ZSM-5, and physical mixture of ZSM-12/ZSM-5. From characterization, it is observed that the ZSM-12/ZSM-5 co-crystalline material is different from that of ZSM-12, ZSM-5, and their physical mixture. Further, the ZSM-12/ZSM-5 co-crystalline zeolite produces the highest content of xylene and has better selectivity for p-xylene than ZSM-12, ZSM-5, and their physical mixture.展开更多
The alkylation of toluene with methanol for the selective formation of p-xylene was systematically studied. Very few studies have been reported on the use of superacids such as heteropolyacids on cheap supports, such ...The alkylation of toluene with methanol for the selective formation of p-xylene was systematically studied. Very few studies have been reported on the use of superacids such as heteropolyacids on cheap supports, such as clay. This article deals with the use of different heteropoly acids （HPAs）, viz, Dodeca-Tungstophosphoric acid [H3PO4.12WO3.xH2O] （TPA）, Dodeca-Molyhdo phosphoric acid ammonium salt hydrate [H12Mo12N3O40P＋aq] （DMAA）, Dodeca-Molyhdo Phosphoric acid （PMA） on clay （MontmoriUonite, K-10） and as such plain clay. This comparative study reveals that 20%PMA/Clay shows 62% toluene conversion and 100% selectivity toward p-xylene.展开更多
文摘The alkylation of toluene with methanol to selective formation of p-xylene has been systematically studied. ZSM-12 （MTW）/ZSM-5 co-crystalline zeolite in 40：60 proportions have been synthesized by the same molar gel composition, but at different temperatures and periods than that of ZSM-12 and ZSM-5, separately. All the prepared samples are characterized by XRD, SEM, BET, and XRF. The activity of toluene alkylation was investigated with a mixture of toluene and methanol as a feed over the ZSM-12, ZSM-12/ZSM-5 co-crystalline, ZSM-5, and physical mixture of ZSM-12/ZSM-5. From characterization, it is observed that the ZSM-12/ZSM-5 co-crystalline material is different from that of ZSM-12, ZSM-5, and their physical mixture. Further, the ZSM-12/ZSM-5 co-crystalline zeolite produces the highest content of xylene and has better selectivity for p-xylene than ZSM-12, ZSM-5, and their physical mixture.
文摘The alkylation of toluene with methanol for the selective formation of p-xylene was systematically studied. Very few studies have been reported on the use of superacids such as heteropolyacids on cheap supports, such as clay. This article deals with the use of different heteropoly acids （HPAs）, viz, Dodeca-Tungstophosphoric acid [H3PO4.12WO3.xH2O] （TPA）, Dodeca-Molyhdo phosphoric acid ammonium salt hydrate [H12Mo12N3O40P＋aq] （DMAA）, Dodeca-Molyhdo Phosphoric acid （PMA） on clay （MontmoriUonite, K-10） and as such plain clay. This comparative study reveals that 20%PMA/Clay shows 62% toluene conversion and 100% selectivity toward p-xylene.
