Friction stir welding(FSW) technique was utilized to weld cast AM50 magnesium alloy plates.The microstructures in the base metal(BM) and the weld joint were observed by optical microscopy.The mechanical properties wer...Friction stir welding(FSW) technique was utilized to weld cast AM50 magnesium alloy plates.The microstructures in the base metal(BM) and the weld joint were observed by optical microscopy.The mechanical properties were investigated by using hardness measurement and tensile test,and the fractographs were observed by scanning electron microscopy.The results show that the microstructure of the base material was characterized by bulk primaryαphase,α-matrix and intermetallic compoundβ(or Mg_(17)Al_(12)),and the weld nugget exhibiting recrystallized microstructure consists ofα-matrix andβphase.The grain size in the weld is smaller than that in the base metal.The hardness of the weld joint is improved but the tensile strength and yield strength,as well as the elongation to failure of the base material decline.The fracture of BM has a rougher surface with more dimples,which is a characteristic of the ductile fracture,whereas the fracture on the nugget reveals a quasi-cleavage feature.The ultimate tensile strength and yield strength of the FSWed AM50 are 86.2%and 94.0%of those of the base metal,respectively.展开更多
基金Project(2007AC4073)supported by Chongqing Munciple Scicnce-Tech Tackle Program,ChinaProject(2008BB0063)supported by theNatural Science Foundation of Chongqing Science and Technology Commission,China
文摘Friction stir welding(FSW) technique was utilized to weld cast AM50 magnesium alloy plates.The microstructures in the base metal(BM) and the weld joint were observed by optical microscopy.The mechanical properties were investigated by using hardness measurement and tensile test,and the fractographs were observed by scanning electron microscopy.The results show that the microstructure of the base material was characterized by bulk primaryαphase,α-matrix and intermetallic compoundβ(or Mg_(17)Al_(12)),and the weld nugget exhibiting recrystallized microstructure consists ofα-matrix andβphase.The grain size in the weld is smaller than that in the base metal.The hardness of the weld joint is improved but the tensile strength and yield strength,as well as the elongation to failure of the base material decline.The fracture of BM has a rougher surface with more dimples,which is a characteristic of the ductile fracture,whereas the fracture on the nugget reveals a quasi-cleavage feature.The ultimate tensile strength and yield strength of the FSWed AM50 are 86.2%and 94.0%of those of the base metal,respectively.