We studied the influence of antimony on the modification rate of the silicon eutectic with sodium and/or strontium for castiig of A1-Si alloys, and introduced controlled Ca and Sb to the system and studied the resulti...We studied the influence of antimony on the modification rate of the silicon eutectic with sodium and/or strontium for castiig of A1-Si alloys, and introduced controlled Ca and Sb to the system and studied the resulting compounds, which were determined to be CazSb and A1Sb. Scanning electron microscopy together with the complementary technique of electron backscatter diffraction (EBSD) were used to characterize the materials. The experimental results provided the basis for us to establish that antimony removal from AI occurs mainly through the reaction (Sb)A1 + 2Ca = Ca^Sb + A1.展开更多
To explore the effect of strontium on the structure of as-cast A356 alloy, the strontium was incorporated to the alloy by metallothermic reduction of SrO where the mineral was added to the melt through the submerged p...To explore the effect of strontium on the structure of as-cast A356 alloy, the strontium was incorporated to the alloy by metallothermic reduction of SrO where the mineral was added to the melt through the submerged powders injection technique. The evaluation of the modification of the eutectie silicon and the chemical analysis of samples were done using optical microscopy (OP) and inductively coupled plasma (ICP), respectively, while microstructural analyses by scanning electron microscopy (SEM), and the injection time was variable. Magnesium was added to the melt to increase the reactivity and reduce the surface tension of the molten aluminum. It was possible to increase the strontium content from 0 to 0.027% after 20 minutes treatment. This concentration was sufficient to bring about full modification structure of eutectic silicon of as cast alloy A 356 and the acceptable quality metallurgical of alloy.展开更多
文摘We studied the influence of antimony on the modification rate of the silicon eutectic with sodium and/or strontium for castiig of A1-Si alloys, and introduced controlled Ca and Sb to the system and studied the resulting compounds, which were determined to be CazSb and A1Sb. Scanning electron microscopy together with the complementary technique of electron backscatter diffraction (EBSD) were used to characterize the materials. The experimental results provided the basis for us to establish that antimony removal from AI occurs mainly through the reaction (Sb)A1 + 2Ca = Ca^Sb + A1.
文摘To explore the effect of strontium on the structure of as-cast A356 alloy, the strontium was incorporated to the alloy by metallothermic reduction of SrO where the mineral was added to the melt through the submerged powders injection technique. The evaluation of the modification of the eutectie silicon and the chemical analysis of samples were done using optical microscopy (OP) and inductively coupled plasma (ICP), respectively, while microstructural analyses by scanning electron microscopy (SEM), and the injection time was variable. Magnesium was added to the melt to increase the reactivity and reduce the surface tension of the molten aluminum. It was possible to increase the strontium content from 0 to 0.027% after 20 minutes treatment. This concentration was sufficient to bring about full modification structure of eutectic silicon of as cast alloy A 356 and the acceptable quality metallurgical of alloy.