The corrosion performances of the as-cast and solution-treated Mg-0.5Zn samples were investigated in 0.9%Na Cl solution and compared.From the electrochemical measurement results and corrosion morphology observations,i...The corrosion performances of the as-cast and solution-treated Mg-0.5Zn samples were investigated in 0.9%Na Cl solution and compared.From the electrochemical measurement results and corrosion morphology observations,it is found that the corrosion resistance of Mg-0.5Zn deteriorated with the extension of solution treatment duration.The main reason was the formation of Fe-Si precipitates with higher Fe concentrations during heat treatment.The Fe-Si precipitates,especially the ones with high Fe contents influenced the corrosion initiation and propagation significantly.In regard of corrosion performance,the solution-treated and then extruded sample was also performing not as good as the cast and then directly extruded sample.展开更多
基金China Scholarship Council for the award of fellowship and funding(201604910527)。
文摘The corrosion performances of the as-cast and solution-treated Mg-0.5Zn samples were investigated in 0.9%Na Cl solution and compared.From the electrochemical measurement results and corrosion morphology observations,it is found that the corrosion resistance of Mg-0.5Zn deteriorated with the extension of solution treatment duration.The main reason was the formation of Fe-Si precipitates with higher Fe concentrations during heat treatment.The Fe-Si precipitates,especially the ones with high Fe contents influenced the corrosion initiation and propagation significantly.In regard of corrosion performance,the solution-treated and then extruded sample was also performing not as good as the cast and then directly extruded sample.