Monolithic bulk metallic glass and glass matrix composites with a relative density above 98%were produced by processing Cu_(46)Zr_(46)Al_(8)(at.%)via selective laser melting(SLM).Their microstructures and mechanical p...Monolithic bulk metallic glass and glass matrix composites with a relative density above 98%were produced by processing Cu_(46)Zr_(46)Al_(8)(at.%)via selective laser melting(SLM).Their microstructures and mechanical properties were systematically examined.B2 CuZr nanocrystals(30-100 nm in diameter)are uniformly dispersed in the glassy matrix when SLM is conducted at an intermediate energy input.These B2 CuZr nanocrystals nucleate the oxygen-stabilized big cube phase during a remelting step.The presence of these nanocrystals increases the structural heterogeneity as indirectly revealed by mircrohardness and nanoindentation measurements.The corresponding maps in combination with calorimetric data indicate that the glassy phase is altered by the processing conditions.Despite the formation of crystals and a high overall free volume content,all additively manufactured samples fail at lower stress than the as-cast glass and without any plastic strain.The inherent brittleness is attributed to the presence of relatively large pores and the increased oxygen content after selective laser melting.展开更多
基金L.Deng acknowledges financial support by the Chinese Scholarship Council(CSC)support by German Research Foundation(DFG)(Nos.PA 2275/4-1,PA2275/6-1 and KO5771/1-1)+1 种基金support by the National Natural Science Foundation of China(Nos.51701213 and 51790484)the National key research and development program(2018YFB0703402)。
文摘Monolithic bulk metallic glass and glass matrix composites with a relative density above 98%were produced by processing Cu_(46)Zr_(46)Al_(8)(at.%)via selective laser melting(SLM).Their microstructures and mechanical properties were systematically examined.B2 CuZr nanocrystals(30-100 nm in diameter)are uniformly dispersed in the glassy matrix when SLM is conducted at an intermediate energy input.These B2 CuZr nanocrystals nucleate the oxygen-stabilized big cube phase during a remelting step.The presence of these nanocrystals increases the structural heterogeneity as indirectly revealed by mircrohardness and nanoindentation measurements.The corresponding maps in combination with calorimetric data indicate that the glassy phase is altered by the processing conditions.Despite the formation of crystals and a high overall free volume content,all additively manufactured samples fail at lower stress than the as-cast glass and without any plastic strain.The inherent brittleness is attributed to the presence of relatively large pores and the increased oxygen content after selective laser melting.