Squeeze casting has become the most competitive casting process in the automotive industry because of its many advantages over high pressure die casting (HPDC). Many squeeze casting R & D and small amount volume m...Squeeze casting has become the most competitive casting process in the automotive industry because of its many advantages over high pressure die casting (HPDC). Many squeeze casting R & D and small amount volume making have been implemented around the world, but the mass production control still exists problem. SPX Contech squeeze casting process P2000 successfully achieved the goal of mass production; it includes lower metal turbulence, less gas entrapment, minimum volumetric shrinkage, and thus less porosity. Like other casting processes, however, the quality of squeeze castings is still sensitive to process control and gate and runner design. Casting defects can form in both die-filling and metal solidification phases. The occurrence of casting defects is directly attributed to improper adjustment or lack of control of process parameters including metal filling velocity, temperature, dwell time, cooling pattern, casting design, and etc. This paper presents examples using P2000 techniques to improve part quality in the following areas: runner & gate design, casting & runner layout in the die, squeeze pin application, high thermal conductivity inserts, cooling/heating systems, spray & lubricant techniques, and part stress calculation from shrinkage or displacement prediction after stress relief.展开更多
文摘Squeeze casting has become the most competitive casting process in the automotive industry because of its many advantages over high pressure die casting (HPDC). Many squeeze casting R & D and small amount volume making have been implemented around the world, but the mass production control still exists problem. SPX Contech squeeze casting process P2000 successfully achieved the goal of mass production; it includes lower metal turbulence, less gas entrapment, minimum volumetric shrinkage, and thus less porosity. Like other casting processes, however, the quality of squeeze castings is still sensitive to process control and gate and runner design. Casting defects can form in both die-filling and metal solidification phases. The occurrence of casting defects is directly attributed to improper adjustment or lack of control of process parameters including metal filling velocity, temperature, dwell time, cooling pattern, casting design, and etc. This paper presents examples using P2000 techniques to improve part quality in the following areas: runner & gate design, casting & runner layout in the die, squeeze pin application, high thermal conductivity inserts, cooling/heating systems, spray & lubricant techniques, and part stress calculation from shrinkage or displacement prediction after stress relief.