Electrochemical capacitor （EC） is a promising energy storage device which can be hybridized with other energy conversion or energy storage devices. One type of ECs is pseudocapacitor made of metal oxides. WO3 is an ...Electrochemical capacitor （EC） is a promising energy storage device which can be hybridized with other energy conversion or energy storage devices. One type of ECs is pseudocapacitor made of metal oxides. WO3 is an inexpensive semiconductor metal oxide which has many applications. However the application of WO3 as an EC material was rarely reported. Therefore in this research EC was prepared from WO3 nanomaterial synthesized by a sol-gel process. The WO3 gel was spin-coated on graphite substrates and calcined at various temperatures of 300~C, 400℃, 500℃ and 600℃ for 1 h. Cyclic voltammetry （CV） measurements were used to observe the capacitive property of the WO3 samples. SEM, XRD, FTIR and Brunauer-Emmett-Teller （BET） analyses were used to characterize the material structures. WO3 calcined at 400~C was proved to have the highest capacitance of 233.63 Fo g^-1 （1869 mFo cm-2） at a scan rate of 2 mVo s-1 in 1 mol/L H2SO4 between potentials -0.4 and 0.4 V vs. SCE. Moreover it also showed the most symmetric CV curves as the indication of a good EC. Hence WO3 calcined at 400℃ is a potential candidate for EC material of pseudocapacitor type.展开更多
基金The financial support from Indonesia Toray Science Foundation （ITSF） through Science and Technology Research Grant （STRG） 2012 is gratefully acknowledged.
文摘Electrochemical capacitor （EC） is a promising energy storage device which can be hybridized with other energy conversion or energy storage devices. One type of ECs is pseudocapacitor made of metal oxides. WO3 is an inexpensive semiconductor metal oxide which has many applications. However the application of WO3 as an EC material was rarely reported. Therefore in this research EC was prepared from WO3 nanomaterial synthesized by a sol-gel process. The WO3 gel was spin-coated on graphite substrates and calcined at various temperatures of 300~C, 400℃, 500℃ and 600℃ for 1 h. Cyclic voltammetry （CV） measurements were used to observe the capacitive property of the WO3 samples. SEM, XRD, FTIR and Brunauer-Emmett-Teller （BET） analyses were used to characterize the material structures. WO3 calcined at 400~C was proved to have the highest capacitance of 233.63 Fo g^-1 （1869 mFo cm-2） at a scan rate of 2 mVo s-1 in 1 mol/L H2SO4 between potentials -0.4 and 0.4 V vs. SCE. Moreover it also showed the most symmetric CV curves as the indication of a good EC. Hence WO3 calcined at 400℃ is a potential candidate for EC material of pseudocapacitor type.