The low-reactivity mold flux with low SiO_(2)content is considered suitable for the continuous casting of high-aluminum steel since it can significantly reduce the reaction between Al in steel and SiO_(2)in mold flux....The low-reactivity mold flux with low SiO_(2)content is considered suitable for the continuous casting of high-aluminum steel since it can significantly reduce the reaction between Al in steel and SiO_(2)in mold flux.However,the traditional low-reactivity mold flux still presents some problems such as high viscosity and strong crystallization tendency.In this study,the co-addition of Li_(2)O and B_(2)O_(3)in CaO–Al_(2)O_(3)–10wt%Si O_(2)based low-reactivity mold flux was proposed to improve properties of mold flux for high-aluminum steel,and the effect of Li_(2)O replacing B_(2)O_(3)on properties of mold flux was investigated.The viscosity of the mold flux with 2wt%Li_(2)O and 6wt%B_(2)O_(3)reached a minimum value of 0.07 Pa·s.The break temperature and melting point showed a similar trend with the viscosity.Besides,the melt structure and precipitation of the crystalline phase were studied using Raman and X-ray diffraction spectra to better understand the evolution of viscosity.It demonstrated that with increasing Li_(2)O content in the mold flux from 0 to 6 wt%,the degree of polymerization of aluminate and the aluminosilicate network structure increased because of increasing Li+released by Li_(2)O,indicating the added Li_(2)O was preferentially associated with Al^(3+)as a charge compensator.The precipitation of LiAlO_(2)crystalline phase gradually increased with the replacement of B_(2)O_(3)by Li_(2)O.Therefore,Li_(2)O content should be controlled below 2wt%to avoid LiAlO_(2)precipitation,which was harmful to the continuous casting of highaluminum steels.展开更多
基金financially supported by the National Science Foundation China (No.U22A20171)the Scinence and Technology Program of Hebei,China (No.20311004D)。
文摘The low-reactivity mold flux with low SiO_(2)content is considered suitable for the continuous casting of high-aluminum steel since it can significantly reduce the reaction between Al in steel and SiO_(2)in mold flux.However,the traditional low-reactivity mold flux still presents some problems such as high viscosity and strong crystallization tendency.In this study,the co-addition of Li_(2)O and B_(2)O_(3)in CaO–Al_(2)O_(3)–10wt%Si O_(2)based low-reactivity mold flux was proposed to improve properties of mold flux for high-aluminum steel,and the effect of Li_(2)O replacing B_(2)O_(3)on properties of mold flux was investigated.The viscosity of the mold flux with 2wt%Li_(2)O and 6wt%B_(2)O_(3)reached a minimum value of 0.07 Pa·s.The break temperature and melting point showed a similar trend with the viscosity.Besides,the melt structure and precipitation of the crystalline phase were studied using Raman and X-ray diffraction spectra to better understand the evolution of viscosity.It demonstrated that with increasing Li_(2)O content in the mold flux from 0 to 6 wt%,the degree of polymerization of aluminate and the aluminosilicate network structure increased because of increasing Li+released by Li_(2)O,indicating the added Li_(2)O was preferentially associated with Al^(3+)as a charge compensator.The precipitation of LiAlO_(2)crystalline phase gradually increased with the replacement of B_(2)O_(3)by Li_(2)O.Therefore,Li_(2)O content should be controlled below 2wt%to avoid LiAlO_(2)precipitation,which was harmful to the continuous casting of highaluminum steels.
