A novel coating on the Mg1Mn alloy was produced by anodic polarization combined with hydrothermal treatment(AP+H)in 0.1 M Na2CO3 solution.The microstructure and protection of the coating were evaluated.The coating con...A novel coating on the Mg1Mn alloy was produced by anodic polarization combined with hydrothermal treatment(AP+H)in 0.1 M Na2CO3 solution.The microstructure and protection of the coating were evaluated.The coating consisted of MgCO3,Mg(OH)2 and MgO,and provided satisfactory protection in 3.5 wt%NaCl with a corrosion rate of 0.07 mm y−1 in 72 h.However,after that period,the corrosion rate of the specimen increased due to the damage of the coating.The failure of the coating was strongly related to the second phase particles(e.g.Zr particles)or impurities in the matrix.The AP+H coating is supposed to be used as a primer coating for Mg applications in kitchen ware,biomedical areas or industry.展开更多
基金supported by the National Natural Science Foundation of China(No.51801168).
文摘A novel coating on the Mg1Mn alloy was produced by anodic polarization combined with hydrothermal treatment(AP+H)in 0.1 M Na2CO3 solution.The microstructure and protection of the coating were evaluated.The coating consisted of MgCO3,Mg(OH)2 and MgO,and provided satisfactory protection in 3.5 wt%NaCl with a corrosion rate of 0.07 mm y−1 in 72 h.However,after that period,the corrosion rate of the specimen increased due to the damage of the coating.The failure of the coating was strongly related to the second phase particles(e.g.Zr particles)or impurities in the matrix.The AP+H coating is supposed to be used as a primer coating for Mg applications in kitchen ware,biomedical areas or industry.