Single-phase face-centered cubic(fcc)medium-and high-entropy alloys(MEAs/HEAs)have high ductility but low yield strength.In this work,the microstructures of single-phase fcc Ni_(2)CoFeV_(0.5) MEAs were tailored by col...Single-phase face-centered cubic(fcc)medium-and high-entropy alloys(MEAs/HEAs)have high ductility but low yield strength.In this work,the microstructures of single-phase fcc Ni_(2)CoFeV_(0.5) MEAs were tailored by cold-rolling and subsequent annealing and typical heterogeneous lamella(HL)structures composed of recrystallized micro-grain lamellae(with an averaged grain size of∼4μm)and nonrecrystallized nano-/ultrafine-grain lamellae were obtained.Tensile tests revealed that most HL samples exhibited excellent strength and ductility synergy.The HL sample with∼23 vol%recrystallized grains annealed at 590℃ for 1 h had a high yield strength of 1120 MPa and a good fracture elongation of 12.3%,which increased by 5%and 46%,respectively compared with those of as-rolled sample.Annealing-induced yield strength increase is attributed to high-density annealing twin boundaries(TBs)in the recrystallized grains,the annihilation of mobile dislocations inside the non-recrystallized grains,and extra heterodeformation-induced strengthening produced by the HL structure.Hall-Petch relationship of Ni_(2)CoFeV_(0.5) MEA can be reasonably described by counting both TBs and grain boundaries,with lattice friction stress of 87.3 MPa and coefficient of 722.8 MPaμm1/2.Our work provides optional and controllable solutions for preparing MEAs/HEAs with excellent mechanical properties by low-cost and high-efficiency thermomechanical treatments.展开更多
基金supported by the National First-rate Discipline Construction Project of Ningxia (Chemical Engineering and Technology)the Major Innovation Projects for Building First-class Universities in China’s Western Region (ZKZD2017003)+2 种基金the University Research Project of Ningxia (NGY2015027)the National Natural Science Foundation of China (21263018)the Project of Science and Technology of Personnel of Study Abroad (Ningxia (2014) 486)~~
基金supported by the National Key R&D Program of China(Grant No.2021YFA1200203)National Natural Science Foundation of China(Grant Nos.51971112,51225102,92163215,52174364,52101143,51731006,and 12202201)+1 种基金Natural Science Foundation of Jiangsu Province Major Project(Grant No.BK20212009)the Fundamental Research Funds for the Central Universities(Grant Nos.30922010202,30922010711,and 30919011405)。
文摘Single-phase face-centered cubic(fcc)medium-and high-entropy alloys(MEAs/HEAs)have high ductility but low yield strength.In this work,the microstructures of single-phase fcc Ni_(2)CoFeV_(0.5) MEAs were tailored by cold-rolling and subsequent annealing and typical heterogeneous lamella(HL)structures composed of recrystallized micro-grain lamellae(with an averaged grain size of∼4μm)and nonrecrystallized nano-/ultrafine-grain lamellae were obtained.Tensile tests revealed that most HL samples exhibited excellent strength and ductility synergy.The HL sample with∼23 vol%recrystallized grains annealed at 590℃ for 1 h had a high yield strength of 1120 MPa and a good fracture elongation of 12.3%,which increased by 5%and 46%,respectively compared with those of as-rolled sample.Annealing-induced yield strength increase is attributed to high-density annealing twin boundaries(TBs)in the recrystallized grains,the annihilation of mobile dislocations inside the non-recrystallized grains,and extra heterodeformation-induced strengthening produced by the HL structure.Hall-Petch relationship of Ni_(2)CoFeV_(0.5) MEA can be reasonably described by counting both TBs and grain boundaries,with lattice friction stress of 87.3 MPa and coefficient of 722.8 MPaμm1/2.Our work provides optional and controllable solutions for preparing MEAs/HEAs with excellent mechanical properties by low-cost and high-efficiency thermomechanical treatments.
