The La-modified Cu-Mn spinel oxide was successfully coated onto honeycomb ceramic by a washcoating method for complete catalytic decomposition of ethyl acetate.The La-modified Cu-Mn oxides were characterized by X-ray ...The La-modified Cu-Mn spinel oxide was successfully coated onto honeycomb ceramic by a washcoating method for complete catalytic decomposition of ethyl acetate.The La-modified Cu-Mn oxides were characterized by X-ray diffraction,X-ray fluorescence,H_(2)-temperature programmed reduction,Brunauer-Emmett-Teller method,field-emission scanning electron microscopy and high-resolution transmission electron microscopy.The effects of different precipitants and rare earth doping on the structure and catalytic performance of the catalysts were investigated.The results show that the CuMn_(2)O_(4) spinel with(NH_(4))_(2)CO_(3) as a precipitant can form a larger specific surface area and a suitable pore size,which is beneficial to the absorption of ethyl acetate.Although the rare earth doping does not significantly change the crystal phase structure of the catalyst,it improves its reducibility and lowers the temperature of the catalytic decomposition.With respect to the catalytic decomposition of ethyl acetate,the rare earth-modified Cu-Mn oxide supported on honeycomb ceramic shows excellent catalytic performance with 100% conversion under the conditions of 239℃,space velocity of 12500 h^(-1) and 1000 ppm.And the ethyl acetate removal rate is still 100% after 1440 min of continuous reaction.展开更多
基金Project supported by Chongqing Science and Technology Bureau(cstc2018jscx-msybX0057,cstc2020j scx-msxm038)Chongqing Science and Technology Bureau Key Research and Development Project(cstc2018jszxzdyfxmX0018)。
文摘The La-modified Cu-Mn spinel oxide was successfully coated onto honeycomb ceramic by a washcoating method for complete catalytic decomposition of ethyl acetate.The La-modified Cu-Mn oxides were characterized by X-ray diffraction,X-ray fluorescence,H_(2)-temperature programmed reduction,Brunauer-Emmett-Teller method,field-emission scanning electron microscopy and high-resolution transmission electron microscopy.The effects of different precipitants and rare earth doping on the structure and catalytic performance of the catalysts were investigated.The results show that the CuMn_(2)O_(4) spinel with(NH_(4))_(2)CO_(3) as a precipitant can form a larger specific surface area and a suitable pore size,which is beneficial to the absorption of ethyl acetate.Although the rare earth doping does not significantly change the crystal phase structure of the catalyst,it improves its reducibility and lowers the temperature of the catalytic decomposition.With respect to the catalytic decomposition of ethyl acetate,the rare earth-modified Cu-Mn oxide supported on honeycomb ceramic shows excellent catalytic performance with 100% conversion under the conditions of 239℃,space velocity of 12500 h^(-1) and 1000 ppm.And the ethyl acetate removal rate is still 100% after 1440 min of continuous reaction.