The FeCrNi alloy powders were used on the dovetail groove of FV520B steel to fabricate the multilayer laser cladding layers. The effects of heat treatment on the microstructure and mechanical properties of FeCrNi laye...The FeCrNi alloy powders were used on the dovetail groove of FV520B steel to fabricate the multilayer laser cladding layers. The effects of heat treatment on the microstructure and mechanical properties of FeCrNi layers were investigated. The results showed that the heat treatment at the temperature ranged from 1073 to 1273 K refined the grains of the substrate materials and removed the soft zone of hardness between the fused zone (FZ) and base material (BM) effectively mainly due to a secondary quench of heat treatment. When the temperature of heat treatment was 1073 K, the maximum ultimate tensile strength (UTS) values of the laser cladding component were obtained. However, the heat treatment at high temperature had a bad effect on wear resistance of coatings at some extent.展开更多
基金Project(51375511)supported by the National Natural Science Foundation of ChinaProject(CDJZR14130008)supported by the Fundamental Research Funds for the Central Universities of China+1 种基金Project(CDJZR13130033)supported by the Fundamental Research Funds for the Central Universities of ChinaProject(CDJZR13130080)supported by the Fundamental Research Funds for the Central Universities of China
文摘The FeCrNi alloy powders were used on the dovetail groove of FV520B steel to fabricate the multilayer laser cladding layers. The effects of heat treatment on the microstructure and mechanical properties of FeCrNi layers were investigated. The results showed that the heat treatment at the temperature ranged from 1073 to 1273 K refined the grains of the substrate materials and removed the soft zone of hardness between the fused zone (FZ) and base material (BM) effectively mainly due to a secondary quench of heat treatment. When the temperature of heat treatment was 1073 K, the maximum ultimate tensile strength (UTS) values of the laser cladding component were obtained. However, the heat treatment at high temperature had a bad effect on wear resistance of coatings at some extent.