2195 Al-Li alloy was deformed through extrusion followed by cold-rolling.The textures of the extruded plate and cold-rolled sheet after solutionization were investigated.The longitudinal strength and precipitates afte...2195 Al-Li alloy was deformed through extrusion followed by cold-rolling.The textures of the extruded plate and cold-rolled sheet after solutionization were investigated.The longitudinal strength and precipitates after T8 aging were measured and observed,respectively.Compared to those in the sheet,T1(Al2 Cu Li)precipitates in the extruded plate after T8 aging are non-uniform,and their incubation time is shorter.The extruded plate after solutionization is not recrystallized and contains 55.28%deformation textures of Brass and S.In the cold-rolled sheet after solutionization,massive recrystallization occurs and S component disappears.Due to the higher fraction of Brass and S textures with higher Schmid factor and lower equivalent sliding system number,the extruded plate possesses an yield strength not higher or even lower,but a tensile strength higher,than the cold-rolled sheet after solutionization.In addition,during the aging after pre-stretch,these textures promote T1 precipitation on preferred sliding planes of cold-rolled sheet and cause its higher yield strength and tensile strength after T8 aging.展开更多
基金Project(2013AA032401)supported by the National High Technology Research and Development Program of China。
文摘2195 Al-Li alloy was deformed through extrusion followed by cold-rolling.The textures of the extruded plate and cold-rolled sheet after solutionization were investigated.The longitudinal strength and precipitates after T8 aging were measured and observed,respectively.Compared to those in the sheet,T1(Al2 Cu Li)precipitates in the extruded plate after T8 aging are non-uniform,and their incubation time is shorter.The extruded plate after solutionization is not recrystallized and contains 55.28%deformation textures of Brass and S.In the cold-rolled sheet after solutionization,massive recrystallization occurs and S component disappears.Due to the higher fraction of Brass and S textures with higher Schmid factor and lower equivalent sliding system number,the extruded plate possesses an yield strength not higher or even lower,but a tensile strength higher,than the cold-rolled sheet after solutionization.In addition,during the aging after pre-stretch,these textures promote T1 precipitation on preferred sliding planes of cold-rolled sheet and cause its higher yield strength and tensile strength after T8 aging.