Preparation and photo-patterning characteristics of organic-inorganic hybrid thin film containing latent pigment by using photo-acid-generator (PAG) and microwave irradiation have been investigated. The acrylic thin f...Preparation and photo-patterning characteristics of organic-inorganic hybrid thin film containing latent pigment by using photo-acid-generator (PAG) and microwave irradiation have been investigated. The acrylic thin film modified with methoxysilane containing PAG was formed on a glass substrate and irradiated with ultraviolet rays to promote sol-gel reaction by catalytic action of acid which was generated from PAG. And then the film was hardened with microwave irradiation, yielding organic-inorganic hybrid polymer film having hardness, highly transparency and strong adhesion with a glass substrate. Since this reaction only occurred in the optically (UV) irradiated regions, by exploiting the difference between the adhesivenesses of these regions photo-irradiated through photomask with a glass substrate, it was possible to form a patterned film with pitch of 100 to 50 μm by a simple lift-off method. A pigment-containing film using latent pigments (with subtractive three primary colors of coloring materials) and a patterned film were prepared, and it was possible to make these films multi-colored by varying the mixing ratio of the pigments. This multi-colored film-preparation method is effective for simply and efficiently forming a color-filter film by applying optical and microwave irradiation.展开更多
文摘Preparation and photo-patterning characteristics of organic-inorganic hybrid thin film containing latent pigment by using photo-acid-generator (PAG) and microwave irradiation have been investigated. The acrylic thin film modified with methoxysilane containing PAG was formed on a glass substrate and irradiated with ultraviolet rays to promote sol-gel reaction by catalytic action of acid which was generated from PAG. And then the film was hardened with microwave irradiation, yielding organic-inorganic hybrid polymer film having hardness, highly transparency and strong adhesion with a glass substrate. Since this reaction only occurred in the optically (UV) irradiated regions, by exploiting the difference between the adhesivenesses of these regions photo-irradiated through photomask with a glass substrate, it was possible to form a patterned film with pitch of 100 to 50 μm by a simple lift-off method. A pigment-containing film using latent pigments (with subtractive three primary colors of coloring materials) and a patterned film were prepared, and it was possible to make these films multi-colored by varying the mixing ratio of the pigments. This multi-colored film-preparation method is effective for simply and efficiently forming a color-filter film by applying optical and microwave irradiation.