Corrosion behaviour and biofouling characteristics of mild steel in three different coastal locations in the Gulf of Mannar,India have been studied over a period of 24 months.Oyster fouling was predominant at Open sea...Corrosion behaviour and biofouling characteristics of mild steel in three different coastal locations in the Gulf of Mannar,India have been studied over a period of 24 months.Oyster fouling was predominant at Open sea-Tuticorin,while barnacle fouling was dominant at both Mandapam and Harbour-Tuticorin.The rate of corrosion for 24 months exposure period was highest at Mandapam,where fouling was minimal.The surface of the mild steel was characterized by etchings&crevices beneath the hard foulers attached on it,at all the test locations.The depth of crevice caused by hard foulers was higher at Open sea-Tuticorin followed by Harbour-Tuticorin and Mandapam.The loss in ultimate tensile strength was more in Open sea-Tuticorin than the other two locations.Corrosion behaviour of mild steel is discussed based on the variation in the biofouling assemblage at the three test locations.展开更多
In the present study an attempt has been made to investigate the relationship between the variations in the fouling assemblage and corrosion behaviour of HSLA steel at three coastal locations in the Gulf of Mannar, In...In the present study an attempt has been made to investigate the relationship between the variations in the fouling assemblage and corrosion behaviour of HSLA steel at three coastal locations in the Gulf of Mannar, India, over a period of 24 months. Oyster fouling was dominant in the Tuticorin open sea, while barnacles were the major foulants in the Tuticorin harbour and Mandapam. The fouling load in the Tuticorin waters was higher when compared to the Mandapam waters. The corrosion rates decreased progressively with the immersion time at all three test locations. In the Tuticorin open sea, the corrosion rates were higher when compared to the other two locations throughout the study period. The surface of the coupons was characterized by crevices beneath the hard foulers in the Tuticorin harbour and Mandapam, whereas in the Tuticorin open sea, the coupons experienced crevices of a tunneling nature. The percentage of the loss of the tensile strength increased with time at all the test locations.展开更多
基金Supported by the Ministry of Environment and Forests,New Delhi(Project Grant No.19-26/2003-RE)
文摘Corrosion behaviour and biofouling characteristics of mild steel in three different coastal locations in the Gulf of Mannar,India have been studied over a period of 24 months.Oyster fouling was predominant at Open sea-Tuticorin,while barnacle fouling was dominant at both Mandapam and Harbour-Tuticorin.The rate of corrosion for 24 months exposure period was highest at Mandapam,where fouling was minimal.The surface of the mild steel was characterized by etchings&crevices beneath the hard foulers attached on it,at all the test locations.The depth of crevice caused by hard foulers was higher at Open sea-Tuticorin followed by Harbour-Tuticorin and Mandapam.The loss in ultimate tensile strength was more in Open sea-Tuticorin than the other two locations.Corrosion behaviour of mild steel is discussed based on the variation in the biofouling assemblage at the three test locations.
基金Supported by the Ministry of Environment and Forests,New Delhi for the Financial Support(Project Grant No.19-26/2003-RE)
文摘In the present study an attempt has been made to investigate the relationship between the variations in the fouling assemblage and corrosion behaviour of HSLA steel at three coastal locations in the Gulf of Mannar, India, over a period of 24 months. Oyster fouling was dominant in the Tuticorin open sea, while barnacles were the major foulants in the Tuticorin harbour and Mandapam. The fouling load in the Tuticorin waters was higher when compared to the Mandapam waters. The corrosion rates decreased progressively with the immersion time at all three test locations. In the Tuticorin open sea, the corrosion rates were higher when compared to the other two locations throughout the study period. The surface of the coupons was characterized by crevices beneath the hard foulers in the Tuticorin harbour and Mandapam, whereas in the Tuticorin open sea, the coupons experienced crevices of a tunneling nature. The percentage of the loss of the tensile strength increased with time at all the test locations.