The deformation behavior of as-built and hot isostatically pressed(HIP)Ti-6Al-4V alloys fabricated using electron beam rapid manufacturing(EBRM)were investigated in this work.The deformation characteristics were chara...The deformation behavior of as-built and hot isostatically pressed(HIP)Ti-6Al-4V alloys fabricated using electron beam rapid manufacturing(EBRM)were investigated in this work.The deformation characteristics were characterized using a laser scanning confocal microscope and electron back-scattered diffraction(EBSD).In the as-built sample,prismatic slip was the main mode of deformation,as well as a small amount of basal slip and cross-slip.Some planar slip lines with large length scales were observed across severalαlamellae.After hot isostatical pressing,prismatic and basal slip were the main mode of deformation,accompanied by abundant cross-slip and multiple slip,and most of the slip lines were blocked within an a lamellae.These differences in deformation behavior were associated with the coarsening of a laths and the more retained p phase after HIP compared to the as-built alloy.More cross-slip and multiple slip can lead to superior elongation-to-failure and a greater strain hardening effect in the HIP alloy compared to the as-built sample.展开更多
基金financially supported by the National Key Research and Development Program of China (No.2017YFB1103100)the Avic Science Foundation of China (No.20175492002)the National Natural Science Foundation of China (No.51801213)
文摘The deformation behavior of as-built and hot isostatically pressed(HIP)Ti-6Al-4V alloys fabricated using electron beam rapid manufacturing(EBRM)were investigated in this work.The deformation characteristics were characterized using a laser scanning confocal microscope and electron back-scattered diffraction(EBSD).In the as-built sample,prismatic slip was the main mode of deformation,as well as a small amount of basal slip and cross-slip.Some planar slip lines with large length scales were observed across severalαlamellae.After hot isostatical pressing,prismatic and basal slip were the main mode of deformation,accompanied by abundant cross-slip and multiple slip,and most of the slip lines were blocked within an a lamellae.These differences in deformation behavior were associated with the coarsening of a laths and the more retained p phase after HIP compared to the as-built alloy.More cross-slip and multiple slip can lead to superior elongation-to-failure and a greater strain hardening effect in the HIP alloy compared to the as-built sample.