Both the production process and the chemical composition of Sx were studied, and the serialization of low carbon ductile iron was also discussed. It was indicated that Sx modifier was sensitive to the carbon equivalen...Both the production process and the chemical composition of Sx were studied, and the serialization of low carbon ductile iron was also discussed. It was indicated that Sx modifier was sensitive to the carbon equivalent (CE) of molten iron and to some alloying elements too. When the CE of molten iron and the contents of alloying elements were changed, the content of Sx must be revised with the change correspondingly. Low carbon ductile iron can be stably changed into the one that non-carbon acicular ferrite and retained austenite (about 25%-28%) by quasi-casting bainitic process of using Sx-2 modifier treated Si-Mn-Cr-Cu-alloyed low carbon molten iron. The austenitic low carbon as-cast ductile iron could be obtained by the Ni-Si-Cr 35 5 2 percent alloys molten iron with less than 2% carbon treated by type Sx-3 modifier. The high-toughness ferritic low carbon as-cast ductile iron which contained more than 85 % ferrite in matrix could be got after the molten iron treated by type Sx-4 modifier, and it’s elongation was more than 10 %.展开更多
After the molten iron composed of 1.2%-2.2%C,1.8%-3.0%,Si is modified by the Sx modifier,which is not composed of traditional spheroidizer but several so-called anti-spherical elements,a new type as-cast low carbon du...After the molten iron composed of 1.2%-2.2%C,1.8%-3.0%,Si is modified by the Sx modifier,which is not composed of traditional spheroidizer but several so-called anti-spherical elements,a new type as-cast low carbon ductile iron with good nodulizing effect and the good combined propertiees can be obtained.展开更多
基金The paper is support by Foundation Key Project of Yunnan:Study on inoculated theory and reliability of low carbon ductileiron, NO. 1999E0004Z
文摘Both the production process and the chemical composition of Sx were studied, and the serialization of low carbon ductile iron was also discussed. It was indicated that Sx modifier was sensitive to the carbon equivalent (CE) of molten iron and to some alloying elements too. When the CE of molten iron and the contents of alloying elements were changed, the content of Sx must be revised with the change correspondingly. Low carbon ductile iron can be stably changed into the one that non-carbon acicular ferrite and retained austenite (about 25%-28%) by quasi-casting bainitic process of using Sx-2 modifier treated Si-Mn-Cr-Cu-alloyed low carbon molten iron. The austenitic low carbon as-cast ductile iron could be obtained by the Ni-Si-Cr 35 5 2 percent alloys molten iron with less than 2% carbon treated by type Sx-3 modifier. The high-toughness ferritic low carbon as-cast ductile iron which contained more than 85 % ferrite in matrix could be got after the molten iron treated by type Sx-4 modifier, and it’s elongation was more than 10 %.
文摘After the molten iron composed of 1.2%-2.2%C,1.8%-3.0%,Si is modified by the Sx modifier,which is not composed of traditional spheroidizer but several so-called anti-spherical elements,a new type as-cast low carbon ductile iron with good nodulizing effect and the good combined propertiees can be obtained.