The diblock copolymers intercalated layered silicate was prepared via a melt dispersion technique. Then the effect of intercalated hybrid as filler on acrylonitrile- butadiene-styrene resin was characterized by X-ray ...The diblock copolymers intercalated layered silicate was prepared via a melt dispersion technique. Then the effect of intercalated hybrid as filler on acrylonitrile- butadiene-styrene resin was characterized by X-ray diffraction, transmission electron microscopy, stress-strain measurements in elongation.展开更多
The semibatch emulsifier-free emulsion copolymerization of methyl methacrylate(MMA and butyl acrylate (BA) in the presence of 2-hydroxyethyl methacrylate (HEMA)initiated by K2S2O8 (PSP) was studied. The latex particle...The semibatch emulsifier-free emulsion copolymerization of methyl methacrylate(MMA and butyl acrylate (BA) in the presence of 2-hydroxyethyl methacrylate (HEMA)initiated by K2S2O8 (PSP) was studied. The latex particles can maintain an appreciablestability during the emulsifier-free emulsion copolymerization of MMA and BA in thepresence of HEMA The average particle diameter increase with an increase of totalsolids content, HEMA content, PSP content, ioniC strength of the system and monomerfeed rate, and decrease with the monomer feed ratio From 3/1(MMA/BA;molar ratio.)to1/3. The stability of this reaction system is improved by adding HEMA as nonioniccomonomer High solids content (50%) latex with monodisperse particle can beobtained using this process.展开更多
基金Chinese Education Ministry Foundation for Nankai University and Tianjin University Joint Academy
文摘The diblock copolymers intercalated layered silicate was prepared via a melt dispersion technique. Then the effect of intercalated hybrid as filler on acrylonitrile- butadiene-styrene resin was characterized by X-ray diffraction, transmission electron microscopy, stress-strain measurements in elongation.
文摘The semibatch emulsifier-free emulsion copolymerization of methyl methacrylate(MMA and butyl acrylate (BA) in the presence of 2-hydroxyethyl methacrylate (HEMA)initiated by K2S2O8 (PSP) was studied. The latex particles can maintain an appreciablestability during the emulsifier-free emulsion copolymerization of MMA and BA in thepresence of HEMA The average particle diameter increase with an increase of totalsolids content, HEMA content, PSP content, ioniC strength of the system and monomerfeed rate, and decrease with the monomer feed ratio From 3/1(MMA/BA;molar ratio.)to1/3. The stability of this reaction system is improved by adding HEMA as nonioniccomonomer High solids content (50%) latex with monodisperse particle can beobtained using this process.