Sm2Fe17-xNbx （x = 0-4） powder was synthesized by HDDR treatment and nitrogenation. The effects of partial Nb substitution for Fe on the structural and magnetic properties of Sm2Fe17-xNbx alloys and their nitlides we...Sm2Fe17-xNbx （x = 0-4） powder was synthesized by HDDR treatment and nitrogenation. The effects of partial Nb substitution for Fe on the structural and magnetic properties of Sm2Fe17-xNbx alloys and their nitlides were investigated. It was seen that Sm2（Fe,Nb）17 phase exists in both annealed and HDDR-treated Sm2Fe17-xNbx alloys. However, its content is decreased with the increase in Nb substitution. In annealed alloys, Sm2（Fe,Nb）17 phase becomes unstable and will dissociate into SmFe2 and Fe-rich phases when x 〉 1.5. With HDDR-treatment, the Nb concentration in recombined Sm2（Fe,Nb）17 phase is decreased, and the content of Fe-rich phases is increased. Sm2Fe17-xNbx powder exhibits dendritic cracks and fine particles with a size of less than 300 nm. In nitrogenated alloys, N atoms mainly enter 2：17-type phase to form Sm2（Fe,Nb）17Ny. Partial Nb atoms in Sm2（Fe,Nb）17Ny phase will be released or excluded by nitrogen atoms. Fe-rich phases increase, and are followed by the amorphous Sm2（Fe,Nb）17Ny phase. Nb substitution for Fe with x = 0.5 and 1.0 in Sm2Fe17-xNbxNy powders increases the coercivity and remanence. But when x is greater than 2.0, Nb substitution will deteriorate the magnetic properties.展开更多
基金This work was financially supported by the National Natural Sciences Foundation of China (No. 50271024) and the Natu-ral Science Foundation of Hebei Province, China (No.501013).
文摘Sm2Fe17-xNbx （x = 0-4） powder was synthesized by HDDR treatment and nitrogenation. The effects of partial Nb substitution for Fe on the structural and magnetic properties of Sm2Fe17-xNbx alloys and their nitlides were investigated. It was seen that Sm2（Fe,Nb）17 phase exists in both annealed and HDDR-treated Sm2Fe17-xNbx alloys. However, its content is decreased with the increase in Nb substitution. In annealed alloys, Sm2（Fe,Nb）17 phase becomes unstable and will dissociate into SmFe2 and Fe-rich phases when x 〉 1.5. With HDDR-treatment, the Nb concentration in recombined Sm2（Fe,Nb）17 phase is decreased, and the content of Fe-rich phases is increased. Sm2Fe17-xNbx powder exhibits dendritic cracks and fine particles with a size of less than 300 nm. In nitrogenated alloys, N atoms mainly enter 2：17-type phase to form Sm2（Fe,Nb）17Ny. Partial Nb atoms in Sm2（Fe,Nb）17Ny phase will be released or excluded by nitrogen atoms. Fe-rich phases increase, and are followed by the amorphous Sm2（Fe,Nb）17Ny phase. Nb substitution for Fe with x = 0.5 and 1.0 in Sm2Fe17-xNbxNy powders increases the coercivity and remanence. But when x is greater than 2.0, Nb substitution will deteriorate the magnetic properties.