The formation process of solid electrolyte interphase(SEI) film on spinel LiMn2O4 electrode surface was studied by electrochemical impedance spectroscopy(EIS) during the initial storage in 1 mol/L LiPF6-EC:DMC:D...The formation process of solid electrolyte interphase(SEI) film on spinel LiMn2O4 electrode surface was studied by electrochemical impedance spectroscopy(EIS) during the initial storage in 1 mol/L LiPF6-EC:DMC:DEC electrolyte and in the subsequent first charge-discharge cycle. It has been demonstrated that the SEI film thickness increased with the increase of storage time and spontaneous reactions occurring between spinel LiMn2O4 electrode and electrolyte can be prevented by the SEI film. In the first charge-discharge cycle succeeding the storage, the electrolyte oxidation coupled with Li-ion insertion is evidenced as the main origin to increase the resistance of SEI film. The results also confirm that the variations of the charge transfer resistance(Rot) with the electrode potential(E) can be well described using a classical equation.展开更多
Layered Li-rich Mn-based oxides are promising cathode materials for Li-ion batteries due to their high capacity and high operation voltage.However,their commercial applications are hindered by irreversible capacity lo...Layered Li-rich Mn-based oxides are promising cathode materials for Li-ion batteries due to their high capacity and high operation voltage.However,their commercial applications are hindered by irreversible capacity loss in the first charge-discharge process,voltage decay during cycling,inefficient cyclability and rate capability.Many attempts have been performed to solve such issues,including the mechanism study and strategies to improve the electrochemical performance.This article provides a brief review and future perspective on the main challenges of the high-capacity Li-rich Mn-based cathodes for Li-ion batteries.展开更多
基金the National Key Basic Research Program of China(No.2002BC211804)
文摘The formation process of solid electrolyte interphase(SEI) film on spinel LiMn2O4 electrode surface was studied by electrochemical impedance spectroscopy(EIS) during the initial storage in 1 mol/L LiPF6-EC:DMC:DEC electrolyte and in the subsequent first charge-discharge cycle. It has been demonstrated that the SEI film thickness increased with the increase of storage time and spontaneous reactions occurring between spinel LiMn2O4 electrode and electrolyte can be prevented by the SEI film. In the first charge-discharge cycle succeeding the storage, the electrolyte oxidation coupled with Li-ion insertion is evidenced as the main origin to increase the resistance of SEI film. The results also confirm that the variations of the charge transfer resistance(Rot) with the electrode potential(E) can be well described using a classical equation.
基金This work was supported by NSFC(21621091)National Key Research and Development of China(2016YFB0100202)+4 种基金Natural Science Foundation of Fujian Province(2015J01063)the support of National Materials Genome Project(2016YFB0700600)National Key R&D Program of China(2016YFB0700600)the Guangdong Innovation Team Project(No.2013N080)Shenzhen Science and Technology Research(Nos.JCYJ20151015162256516,JCYJ20150729111733470 and JCYJ20160226105838578)。
文摘Layered Li-rich Mn-based oxides are promising cathode materials for Li-ion batteries due to their high capacity and high operation voltage.However,their commercial applications are hindered by irreversible capacity loss in the first charge-discharge process,voltage decay during cycling,inefficient cyclability and rate capability.Many attempts have been performed to solve such issues,including the mechanism study and strategies to improve the electrochemical performance.This article provides a brief review and future perspective on the main challenges of the high-capacity Li-rich Mn-based cathodes for Li-ion batteries.