The increasing demand for iron ore in the world causes the continuous exhaustion of magnetite resources.The utilization of high-phosphorus iron ore becomes the focus.With calcium carbonate(CaCO_(3)),calcium chloride(C...The increasing demand for iron ore in the world causes the continuous exhaustion of magnetite resources.The utilization of high-phosphorus iron ore becomes the focus.With calcium carbonate(CaCO_(3)),calcium chloride(CaCl_(2)),or calcium sulfate(CaSO_(4))as additive,the process of direct reduction and phosphorus removal of high-phosphorus iron ore(phosphorus mainly occurred in the form of Fe_(3)PO_(7) and apatite)was studied by using the technique of direct reductiongrinding-magnetic separation.The mechanism of calcium compounds to reduce phosphorus was investigated from thermodynamics,iron metallization degree,mineral composition and microstructure.Results showed that Fe_(3)PO_(7) was reduced to elemental phosphorus without calcium compounds.The iron-phosphorus alloy was generated by react of metallic iron and phosphorus,resulting in high phosphorus in reduced iron products.CaCO_(3) promoted the reduction of hematite and magnetite,and improved iron metallization degree,but inhibited the growth of metallic iron particles.CaCl_(2) strengthened the growth of iron particles.However,the recovery of iron was reduced due to the formation of volatile FeCl_(2).CaSO_(4) promoted the growth of iron particles,but the recovery of iron was drastically reduced due to the formation of non-magnetic FeS.CaCO_(3),CaCl_(2) or CaSO_(4) could react with Fe_(3)PO_(7) to form calcium phosphate(Ca_(3)(PO_(4))_(2)).With the addition of CaCO_(3),Ca_(3)(PO_(4))_(2) was closely combined with fine iron particles.It is difficult to separate iron and phosphorus by grinding and magnetic separation,resulting in the reduced iron product phosphorus content of 0.18%.In the presence of CaCl_(2) or CaSO_(4),the boundary between the generated Ca_(3)(PO_(4))_(2) and the metallic iron particles was obvious.Phosphorus was removed by grinding and magnetic separation,and the phosphorus content in the reduced iron product was less than 0.10%.展开更多
Beach titanomagnetite(TTM)provides a cheap alternative source of Fe and Ti,but this ore is difficult to process to make suitable concentrates for the blast furnace.Recently studies showed that it is feasible to separa...Beach titanomagnetite(TTM)provides a cheap alternative source of Fe and Ti,but this ore is difficult to process to make suitable concentrates for the blast furnace.Recently studies showed that it is feasible to separate Fe and Ti by coal-based direct reduction.In this study,beach TTM was selected as the research object,the effects of reducing agents on reducing atmosphere in coal-based direct reduction of beach TTM were analyzed,and the role of volatiles was also studied.The results showed that when bitumite and coke were used as reducing agents of TTM,the CO produced from volatiles was involved in the reduction reaction,and the generated CO_(2) provided the raw material for the reaction of TTM.The reduction effect of bitumite was better than that of coke.The reason is that bitumite+TTM had a higher gas generation rate and produced a higher CO partial pressure,while coke+TTM had a lower gas generation rate and produced a lower CO partial pressure.When graphite was used as a reducing agent,there was a solid-solid reaction in the early stage in the reaction.With the continuous accumulation of CO_(2),the Boudouad reaction started and accelerated.Graphite+TTM also produced a higher CO partial pressure.展开更多
基金Projects(51874017,52174236)supported by the National Natural Science Foundation of China。
文摘The increasing demand for iron ore in the world causes the continuous exhaustion of magnetite resources.The utilization of high-phosphorus iron ore becomes the focus.With calcium carbonate(CaCO_(3)),calcium chloride(CaCl_(2)),or calcium sulfate(CaSO_(4))as additive,the process of direct reduction and phosphorus removal of high-phosphorus iron ore(phosphorus mainly occurred in the form of Fe_(3)PO_(7) and apatite)was studied by using the technique of direct reductiongrinding-magnetic separation.The mechanism of calcium compounds to reduce phosphorus was investigated from thermodynamics,iron metallization degree,mineral composition and microstructure.Results showed that Fe_(3)PO_(7) was reduced to elemental phosphorus without calcium compounds.The iron-phosphorus alloy was generated by react of metallic iron and phosphorus,resulting in high phosphorus in reduced iron products.CaCO_(3) promoted the reduction of hematite and magnetite,and improved iron metallization degree,but inhibited the growth of metallic iron particles.CaCl_(2) strengthened the growth of iron particles.However,the recovery of iron was reduced due to the formation of volatile FeCl_(2).CaSO_(4) promoted the growth of iron particles,but the recovery of iron was drastically reduced due to the formation of non-magnetic FeS.CaCO_(3),CaCl_(2) or CaSO_(4) could react with Fe_(3)PO_(7) to form calcium phosphate(Ca_(3)(PO_(4))_(2)).With the addition of CaCO_(3),Ca_(3)(PO_(4))_(2) was closely combined with fine iron particles.It is difficult to separate iron and phosphorus by grinding and magnetic separation,resulting in the reduced iron product phosphorus content of 0.18%.In the presence of CaCl_(2) or CaSO_(4),the boundary between the generated Ca_(3)(PO_(4))_(2) and the metallic iron particles was obvious.Phosphorus was removed by grinding and magnetic separation,and the phosphorus content in the reduced iron product was less than 0.10%.
基金Project(52104257)supported by the National Natural Science Foundation of China。
文摘Beach titanomagnetite(TTM)provides a cheap alternative source of Fe and Ti,but this ore is difficult to process to make suitable concentrates for the blast furnace.Recently studies showed that it is feasible to separate Fe and Ti by coal-based direct reduction.In this study,beach TTM was selected as the research object,the effects of reducing agents on reducing atmosphere in coal-based direct reduction of beach TTM were analyzed,and the role of volatiles was also studied.The results showed that when bitumite and coke were used as reducing agents of TTM,the CO produced from volatiles was involved in the reduction reaction,and the generated CO_(2) provided the raw material for the reaction of TTM.The reduction effect of bitumite was better than that of coke.The reason is that bitumite+TTM had a higher gas generation rate and produced a higher CO partial pressure,while coke+TTM had a lower gas generation rate and produced a lower CO partial pressure.When graphite was used as a reducing agent,there was a solid-solid reaction in the early stage in the reaction.With the continuous accumulation of CO_(2),the Boudouad reaction started and accelerated.Graphite+TTM also produced a higher CO partial pressure.