To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-f...To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-furnace carbon slag(BOF C) and electric-arc-furnace stainless steel slag(EAF S). Moreover, we studied the standard consistency, setting time and the effect of the slag replacement ratios on the fluidity and compressive strength of blended cement mortar. The experimental results showed that BOF C had higher alkalinity, higher pH value and more hydraulic phases than EAF S. Both types of slag showed water reduction effect due to its high fineness. Neat BOF C paste showed flash set and acceleration in the initial setting time of blended cement especially at high slag proportions. However, EAF S prolonged the setting time of blended cement even at low slag proportions. The pH values for blended cement contained 50% BOF C or EAF S were lower than those of pure cement paste. Despite of slag type, compressive strength gradually decreased with increasing slags content. The strength of BOF C mortar was higher than that of EAF S mortar with the same replacement ratio for the same age. Slag activity index demonstrated that BOF C and EAF S conformed to the Chinese National Standard(GB/T 20491-2006) requirements for steel slag as grade one and grade two, respectively.展开更多
基金The Scholarship Supported by the China Scholarship Councilthe Technical Research Program from NV Bekaert SA of Belgiumthe National Natural Science Foundation of China(No.50908047)
基金Funded by the National Natural Science Foundations of China(Nos.51378113 and 51438003)the Plan of Six Peak Talents in Jiangsu Province(No.JZ-004)Partly Supported by the National Basic Research Program of China(973 Program,No.2015CB655102)
文摘To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-furnace carbon slag(BOF C) and electric-arc-furnace stainless steel slag(EAF S). Moreover, we studied the standard consistency, setting time and the effect of the slag replacement ratios on the fluidity and compressive strength of blended cement mortar. The experimental results showed that BOF C had higher alkalinity, higher pH value and more hydraulic phases than EAF S. Both types of slag showed water reduction effect due to its high fineness. Neat BOF C paste showed flash set and acceleration in the initial setting time of blended cement especially at high slag proportions. However, EAF S prolonged the setting time of blended cement even at low slag proportions. The pH values for blended cement contained 50% BOF C or EAF S were lower than those of pure cement paste. Despite of slag type, compressive strength gradually decreased with increasing slags content. The strength of BOF C mortar was higher than that of EAF S mortar with the same replacement ratio for the same age. Slag activity index demonstrated that BOF C and EAF S conformed to the Chinese National Standard(GB/T 20491-2006) requirements for steel slag as grade one and grade two, respectively.
