The effect of dispersion with different weight fractions of Al2O3 particles in metallic matrices （AI/Mg/Ti/Cu） fabricated by powder metallurgy was investigated. In the case of 15 wt% Al2O3 reinforced composites, pea...The effect of dispersion with different weight fractions of Al2O3 particles in metallic matrices （AI/Mg/Ti/Cu） fabricated by powder metallurgy was investigated. In the case of 15 wt% Al2O3 reinforced composites, peak hardness was attained which subsequently decreased with increasing the content of Al2O3. A correlation between the microhardness and nanomechanical properties at submicron scale was examined for all the composites. Specific strength and specific modulus were measured in order to figure out the performance of the composites.展开更多
文摘The effect of dispersion with different weight fractions of Al2O3 particles in metallic matrices （AI/Mg/Ti/Cu） fabricated by powder metallurgy was investigated. In the case of 15 wt% Al2O3 reinforced composites, peak hardness was attained which subsequently decreased with increasing the content of Al2O3. A correlation between the microhardness and nanomechanical properties at submicron scale was examined for all the composites. Specific strength and specific modulus were measured in order to figure out the performance of the composites.