The sliding wear behaviors of a single layer AI2O3-30 wt pct ZrO2, a double layer AI2O3-30 wt pct ZrO2/Ni-Cr and a single layer AI2O3-13 wt pct TiO2 coating deposited on low carbon steel by plasma spraying were invest...The sliding wear behaviors of a single layer AI2O3-30 wt pct ZrO2, a double layer AI2O3-30 wt pct ZrO2/Ni-Cr and a single layer AI2O3-13 wt pct TiO2 coating deposited on low carbon steel by plasma spraying were investigated under lubricated conditions with various normal loads. The plastic deformation, detachment and pull out of splats were involved in the wear process of the studied coatings under test conditions. Crack propagation was found in AI2O3-13 wt pct TiO2 under loads of 70 and 100 N and in AI2O3-30 wt pct ZrO2/Ni-Cr under a load of 130 N. While increasing the normal load, the wear rates of AI2O3-30 wt pct ZrO2 and AI2O3-30 wt pct ZrO2/Ni-Cr slightly increased, the wear rate of AI2O3-13 wt pct TiO2 increased rapidly. The results showed that the Ni-Cr bonding layer improved the wear resistance of the coating system even it is relatively thin compared with the outer coating layer. The influence of this bonding layer on wear behavior of the coating increased as increasing the normal load.展开更多
The fretting characteristics of TiN coated Zircaloy-4 tube were investigated experimen-tally. The fretting experiment was performed using TIN coated Zircaloy-4 tube as the fuel rod clad-ding material and uncoated Zirc...The fretting characteristics of TiN coated Zircaloy-4 tube were investigated experimen-tally. The fretting experiment was performed using TIN coated Zircaloy-4 tube as the fuel rod clad-ding material and uncoated Zircaloy-4 tube as one of grids. TIN coating is probably one of the mostfrequently and successfully used PVD coatings for the mitigation of fretting. In this study, TiN coat-ing by PVD was employed for improvement of Zircaloy-4 tube fretting characteristics. The frettingtester was designed and manufactured for this experiment. The number of cycles, slip amplitudeand normal load were selected as main factors of fretting. The results of this research showed thatthe wear volume of TiN coated Zircaloy-4 tube increased as number of cycles, normal load andslip amplitude increase but the quantity of volume was lower than the case of uncoated Zircaloy-4tube pairs.展开更多
文摘The sliding wear behaviors of a single layer AI2O3-30 wt pct ZrO2, a double layer AI2O3-30 wt pct ZrO2/Ni-Cr and a single layer AI2O3-13 wt pct TiO2 coating deposited on low carbon steel by plasma spraying were investigated under lubricated conditions with various normal loads. The plastic deformation, detachment and pull out of splats were involved in the wear process of the studied coatings under test conditions. Crack propagation was found in AI2O3-13 wt pct TiO2 under loads of 70 and 100 N and in AI2O3-30 wt pct ZrO2/Ni-Cr under a load of 130 N. While increasing the normal load, the wear rates of AI2O3-30 wt pct ZrO2 and AI2O3-30 wt pct ZrO2/Ni-Cr slightly increased, the wear rate of AI2O3-13 wt pct TiO2 increased rapidly. The results showed that the Ni-Cr bonding layer improved the wear resistance of the coating system even it is relatively thin compared with the outer coating layer. The influence of this bonding layer on wear behavior of the coating increased as increasing the normal load.
文摘The fretting characteristics of TiN coated Zircaloy-4 tube were investigated experimen-tally. The fretting experiment was performed using TIN coated Zircaloy-4 tube as the fuel rod clad-ding material and uncoated Zircaloy-4 tube as one of grids. TIN coating is probably one of the mostfrequently and successfully used PVD coatings for the mitigation of fretting. In this study, TiN coat-ing by PVD was employed for improvement of Zircaloy-4 tube fretting characteristics. The frettingtester was designed and manufactured for this experiment. The number of cycles, slip amplitudeand normal load were selected as main factors of fretting. The results of this research showed thatthe wear volume of TiN coated Zircaloy-4 tube increased as number of cycles, normal load andslip amplitude increase but the quantity of volume was lower than the case of uncoated Zircaloy-4tube pairs.
